PURPOSES : This purpose of this study is to analyze the effect to autogenous shrinkage of the top-layer material of a two-lift concrete pavement mixing both silica fume and polymer powder. METHODS: The bottom-layer of a two-lift concrete pavement was paved with original portland cement (OPC) with a 20~23 cm thickness. Additionally, the top-layer which is directly exposed to the environment and vehicles was paved with a high-performance concrete (HPC) with a 7~10 cm thickness. These types of pavements can achieve a long service life by reducing joint damage and increasing the abrasion and scaling resistance. In order to integrate the different bottom and top layer materials, autogenous shrinkage tests were performed in this study according to the mixing ratio of silica fume and polymer powder, which are the admixture of the top-layer material. RESULTS: Autogenous shrinkage decreased when polymer powder was used in the mix. Contrary to this, autogenous shrinkage tended to rise with increasing silica fume content. However, the effects were not significant when small amounts of polymer powder were used (3% and 11%). CONCLUSIONS : The durability and compressive strength increase when silica fume is used in the mix. The flexural strength considerably increases and autogenous shrinkage of concrete decreases when polymer powder is used in the mix. As seen from above, the proper use of these materials improves not only durability, but also autogenous shrinkage, leading to better shrinkage crack control in the concrete.

Ultra high performance concrete which has recently been studied was developed to complement the brittle behaviour and dynamic uppermost limit of high strength concrete. Fiber reinforced concrete which mixed steel fiber is receiving attention as an alternative about this and is being developed to complement the disadvantages of high strength concrete including lower toughness coefficients and crack resistance and spalling in fires. Review about fiber reinforced ultra high strength concrete that this study tries to treat includes reduction of self shrinkage generated by high cement content per unit volume of concrete, evaluation of compression and tension strength to lower internal and external spalling resistance and fragility factors of member of framework, and flow characteristics of concrete which doesn't harden according to steel fiber amounts and used materials. As the result, the more fiber reinforcement increases, the more compression and tensile strength increase and deformation control of cement matrix and improvement of energy absorption ability showed the great effect in shrinkage reduction.

초속경 라텍스개질 콘크리트(VES-LMC)를 포함한 고성능 콘크리트는 낮은 물-시멘트비, 높은 결합재량 및 고성능감수제의 사용 등으로 인해 자기수축(Autogenous Shrinkage)이 1종 콘크리트(OPC)보다 크게 나타난다. 초속경 라텍스개질 콘크리트의 배합특성은 낮은 물-시멘트비(0.38), 높은 단위시멘트량(390kg/m3) 및 라텍스첨가(단위시멘트량 대비 15%)로 구성되므로, 자기수축이 크게 발생할 수 있고, 또한 콘크리트 타설 후 3시간 이내에 발생하는 급격한 수분소산(Water Dissipation)과 수분증발은 자기수축을 증가시킬 수 있다. 본 논문의 목적은 현장에서 작업시간 확보를 목적으로 사용되는 지연제 첨가량 변화에 따른 초기수축, 온도변형 및 자기수축을 평가하는 것이다. 실험결과 지연제의 첨가는 콘크리트의 최대 수화열에 영향을 미치지 않는 것으로 나타났으며, 초속경 라텍스개질 콘크리트의 초기 팽창은 일부 자기팽창의 영향이 있기는 하지만 대부분이 열팽창에 기인하는 것으로 나타났다. 지연제 첨가량이 증가함에 따라 자기수축이 감소하는 것으로 나타났지만, 지연제의 과도한 사용은 과도한 초기 팽창을 일으킬 수 있으므로 현장조건을 고려하여 신중하게 결정되어야 한다.

현대사회의 급격한 도시화 및 인구밀도 증가로 인하여 고성능 재료를 사용한 고강도 콘크리트의 수요가 증가하고 있으며 고강도 콘크리트가 갖는 자기수축 특성은 콘크리트 내구성에 심각한 문제를 초래할 가능성이 크다. 본 연구에서는 고강도 콘크리트의 자기수축 특성 저감을 위하여 고흡수성 폴리머(SAP: Super absorbent polymer)를 사용하였으며 바인더 대비 0%, 0.3%, 0.5% 첨가한 시험체를 각각 제작하여 매립형 스트레인게이지를 이용하여 수축량을 계측 및 비교하였다. 실험결과 SAP를 0.3%, 0.5% 첨가한 실험체는 SAP를 첨가하지 않은 실험체 보다 수축량이 각각 약 11% 와 34% 감소 하였으며 이에따라 SAP의 첨가는 고강도 콘크리트의 자기수축 저감에 효과가 있는 것으로 나타났다.

The rate of autogenous shrinkage (AS) development is a fundamental factor that highly influence the crack risk in low water cement mortar. Internal curing (IC) by using SAP has been used to reduce the AS in low water cement mortar and consequently mitigates the high risk of early-age cracking. Super absorbent polymers (SAP) supply additional IC water for hydration of mortar and as a result the effect of self-desiccation was minimized when the amount of internal water reduced. A series of autogenous shrinkage tests were performed considering two different SAP particle sizes in a constant curing temperature and humidity. The results indicated that IC method by using SAP fundamentally solved the problem of autogenous shrinkage in a low water cement ratio mortar.

고로슬래그 미분말은 공학적으로 우수한 건설산업 부산물이며, 최근들어 환경부하 저감 및 사용 활성화를 위해 대단위 슬래그 치 환 콘크리트가 많이 연구되고 있다. 본 연구에서는 목표 강도를 50 MPa로 설정하고 고로슬래그미분말 치환률을 65%로 고려한 대단위 치환 슬 래그 콘크리트를 제조하여 건조수축특성과 초지재령 특성을 평가하였다. 이를 위해 3 수준의 콘크리트를 제조하였으며, 슬럼프 플로우, 강도, 건조 및 자기수축에 대한 실험을 수행하였다. 실험결과, 보통 포틀랜트 시멘트를 100% 함유한 콘크리트(OPC 100)에 비하여 재령 7일전의 강 도는 약간 감소하였으나, 슬래그 치환 배합은 수화에 필요한 충분한 자유수를 가졌으므로 28일 재령에서는 우수한 강도 발현을 나타내었다. 또 한 재령 3일까지 큰 자기수축으로 인하여, OPC 100 배합에서는 건조수축이 크게 평가되었지만, 65% 고로슬래그 미분말을 치환한 배합에서는 초기재령의 자기수축 성능이 개선되어 우수한 건조수축거동을 나타내었다. 특히 단순 질량 치환배합(BS 65)보다 물-결합재비(0.27)와 단위수 량(163kg/m3)을 낮춘 OPTBS 65에서 더욱 우수한 건조수축 및 자기수축 거동을 나타내었다.

This study investigates the autogenous shrinkage of morta that contains shrinkage reducing agent (SRA) It is observed that the autogenous shrinkage of mortar was about 300με at 6 days after casting. The SRA reduces the autogenous shrinkage by an half, but unexpected expansion was observed between 1 and 2 days after casting.

The influence of micro-fiber on the autogeneous shrinkage of mortar were explored in this study. Mixtures with 0.4 of W/C are used in the test. Test results show that PVA fiber that added 2% in the mixture does not influence the autogenous shrinkage of mortar because the autogenous shrinkage causes an uniform volume changes of mortar.

In this study, it evaluates autogenous Shrinkage of high strength concrete with polymix fiber and type of aggregate. Consequently, When concrete is mixed with limestone aggregate and spalling prevention fiber, Compressive strength, modulus of elasticity and autogenous shrinkage was better.

본 연구는 대형․대단면 지하공간에 적용하기 위한 고강도 콘크리트의 개발 및 적용을 위한 연구의 일환으로 50MPa급의 고강도 콘크리트의 제조를 위해 플라이애쉬와 고로슬래그미분말의 치환에 따른 최적 배합을 선정하고, 비구속 수축 실험과 수축균열 실험을 통해 정량적으로 평가하였다. 콘크리트의 압축강도는 전 배합이 7일 재령에서 30MPa을 넘었고, 28일 재령에서는 설계강도를 모두 안정적으로 획득하였다. 고강도 콘크리트에 고로슬래그를 사용할 경우 자기수축량이 커지고, 다량 치환할 경우 수축변형이 증가하고 강도발현이 지연되어 수축에 의한 균열 발생의 우려가 있다. 혼화재를 다량 치환한 고강도 콘크리트 배합은 수화반응과 건조 효과에 영향을 주는 초기 재령의 양생 조건에 대한 검토가 필요하다.

고성능 콘크리트의 자기수축은 초기균열을 유도할 수 있기 때문에 내구성 측면에서 매우 중요하다. 이에 따라, 본 연구에서는 실험을 통해 혼화재료를 혼입한 고성능 콘크리트의 자기수축 특성을 분석한 후 예측모델을 제안하였다. 이를 위해 다양한 실험변수를 가진 시편에 대해 광범위한 실험을 수행하였다. 주요 실험변수는 혼화재료의 종류 및 혼입률로 설정하였으며 물-시멘트비는 30%로 고정하였다. 실험결과 플라이애시를 치환한 경우에는 자기수축량이 다소 감소하였으며, 고로슬래그를 사용한 경우에는 자기수축이 증가하였다. 또한, 수축저감제 및 팽창재의 혼입량이 클수록 고성능 콘크리트의 자기수축은 감소하는 경향을 보였다. 한편, 본 논문에서는 회귀분석을 통해 혼화재료를 사용한 고성능 콘크리트의 자기수축 예측식을 제안하였으며, 제안된 자기수축 예측식은 실험결과와 비교적 일치하였다