WC-6wt%Co hard metal powders were sintered by a 2.45 GHz multimode microwave applicator in Ar atmosphere. Microwave sintering of WC-6wt%Co powder lowered the sintering temperature and shortened the processing time in less than two hours than by a conventional method. Microstructures of the sintered specimen were studied with scanning electron microscope (SEM) and no abnormal grain growth was observed. Mechanical properties were similar to the values of the specimens sintered by a conventional method. Specimen sintered at 135 for 30 minutes ,hewed 99%, 20.5 GPa and 8.1 MPa of theoretical density, hardness and fracture strength, respectively.

하부 성층권 온도의 추세에 대한 위성관측과 모델 결과들의 상대적인 정확성을 평가하기 위하여 두 종류의 위성관측 MSU 채널 4(57.95GHz) 밝기온도 자료들과 1981∼1993년 기간의 두 종류의 대순환 모델(ECMWF and GEOS) 재분석 자료들을 시계열 회귀분석으로 상호 비교하였다. 1980∼1999년 기간의 위성자료는 이 연구에서 유도된 직하점 MSU4와 여러 주사각에서 유도된 SC4(Spencer and Christy, 1993)이다. 위 기간에 전지구에 대한 MSU 하부 성층권 온도는 화산폭발과 관련된 냉각화 경향(-0.35K/decade)을 보였으며, 이러한 경향은 육지보다 해양에서 1.2배 컸다. 자료들의 공통 기간(1981∼1993년)에 대한 하부 성층권 온도의 아노말리는 두 종류 관측자료와 GEOS에서 전지구적으로 냉각화 경향(-0.14∼-0.42K/decade)을 보였으나, ECMWF는 북반구를 제외하고 온난화(0.06K/decade)를 보였다. 온도 연주기는 SC4를 제외하고 다른 세 종류 자료에서 유사한 위상과 함께 현저하였다. 온도 추세에 대한 95%신뢰도 조사에서 MSU 채널 4의 하부 성층권 온도에 대한 신뢰도가 채널 2(53.74GHz)의 중간 대류권 온도보다 더 낮았다. 또한 두 기층 사이의 온도 추세 감율이 북반구 육지에서 가장 컸다. MSU4에 대한 SC4 및 모델 재분석 결과들의 상관은 전지구의 경우에 SC4(r=0.96)에서 가장 높았고, ECMWF(r=0.61)에서 가장 낮았다. 한반도의 경우에는 GEOS에서 가장 높았고(r=0.88), ECMWF에서 가장 낮았다(r=0.73). MSU4에 대한 SC4, ECMWF의 상관은 아열대 제트류가 위치하는 30˚ 위도대에서 낮았으나(r〈0.6) 그 외의 지역에서는 대체로 높았다(r〉0.6). 한반도 부근에서 하부 성층권 온도의 냉각화 경향은 모든 자료에서 공통적으로 나타났다. 이러한 추세는 SC4(-0.82K/decade)에서 가장 컸으며, MSU4(-0.38K/decade), GEOS(-0.28K/decade), ECMWF(-0.07K/decade) 순으로 나타났다.

마이크로파 유전체의 품질계수 측정에 사용되는 cavity resonator 방법에 대하여 실제 측정 결과와 전자기 시뮬레이션엔 의한 결과를 비교하였다. 시뮬레이션 기법을 이용하여 마이크로파 유전체의 산란계수 S12 를 실제로 측정한 간과 시뮬레이션에 의해 구해진 값을 비교하였으며 마이크로파 유전체 내부에 기공이 있는 경우와 유전율이 다른 이차상이 존재할 때 마이크로파 품질계수가 어떻게 변화하는지를 검토하였다. 시뮬레이션을 통하여 기본 공진 모드인 TE01δ모드를 쉽게 찾을 수 있었으며 기공 및 이차상에 의한 품질계수의 저하를 정성적으로 확인할 수 있었다

(Zr(sub)0.8Sn(sub)0.2)TiO4세라믹스와 소결조제로서 (B2O3.Li2O)의 첨가에 따른 마이크로파 유전특성 및 미세구조에 미치는 영향에 대하여 연구하였다. 1.0 mol.% Sb2O(sub)5를 첨가하고 1300˚C에서 5시간 소결한 (Zr(sub)0.8Sn(sub)0.2)TiO4세라믹스의 경우 (B2O3.Li2O)첨가량 증가에 따라 치밀화 및 결정립 성장에 의해 유전상수와 Q.f값은 증가하여 첨가량이 0.35wt.%에서 최대값인 38과 59,000을 각각 나타내었으며, 0.50wt.% 이상 첨가한 경우에서는 제 2상의 생성으로 인하여 감소하였다. 1.0 mol% Sb2O(sub)5와 0.35wt.% (B2O3.Li2O)를 첨가한 (Zr(sub)0.8Sn(sub)0.2)TiO4세라믹스를 1250˚C와 1350˚C에서 5시간 소결한 경우에는 각각 미반응 TiO2의 존재와 과대입자성장에 의한 결정립내기공의 생성으로 인하여 마이크로파 유전특성은 저하되었다.

재래식과 마이크로파 열원으로 알루미나 기판을 PbO-ZnO-B2O3계 유리로 봉착하였을 때, 봉착용 유리의 결정화 거동 및 알루미나 기판과의 봉착상태를 조사하였다. 재래식 열처리된 시편에 비하여 마이크로파 열처리된 시편은 짧은 시간과 낮은 온도에서 열처리 되었음에도 불구하고 모유리 내에서 PbTiO3 결정이 잘 성장하였고, 높은 결정화를 보여주었다. 또한, 마이크로파 봉착 시편은 양호한 상태를 보여주었고, 봉착 곡강도는 거의 비슷하였다.

(1-x)CaTi O3-xLa(Z n12/ Ti12/) O3의 마이크로 유전특성을 조사하였다. x가 증가함에 따라 비유전율과 공진주파수의 온도계수는 감소하였으며, Qㆍ f0는 증가하였다. 그 결과 x=0.5인 (C a0.5L a0.5)( Ti0.75Z n0.25) O3의 조성에서 εr=51, Qㆍ f0=38,000 (at 7 GHz), τf=+5ppm/˚C의 유전특성이 나타났다. (C a0.5L a0.5)( Ti0.75Z n0.25) O3조성의 소결온도를 저하시키기 위하여 B i2 O3를 주조성으로한 소결체를 첨가하여 소결 및 유전특성을 조사하였다. 1wt% 0.76B i2 O3-0.24NiO가 첨가된 경우 소결온도는 150˚C 낮아졌으며, 비유전율 (εr), 공진주파수의 온도계수(τf), Qㆍ f0가 각각 50+5ppm/˚C, 35,000인 마이크로파 유전특성이 얻어졌다. 또한 3wt%의 0.76B i2 O3-0.24NiO가 첨가된 경우 소결온도는 200˚C 저하되었고, 비유전율 (εr)과 공진주파수의 온도계수 (τf)는 변하기 않았으나, Qㆍ f0값이 38,000에서 25,000으로 저하되었다. 25,000으로 저하되었다.되었다.되었다.되었다.

CuO의 첨가가 BiNbO4 세라믹스의 마이크로파 유전특성과 소결거동에 미치는 영향에 대하여 연구하였다. CuO의 첨가량이 증가함에 따라 액상의 생성에 의해 소결성이 증가하여 시편의 밀도는 증가하며 유전상수는 소결온도가 증가함에 따라 증가하는 경향을 보였다. Qxfo값은 CuO 첨가량이 0.065wt%이고 소결온도가 940˚C일 때 최대값을 나타내며 그 이상 CuO 첨가량을 증가하였다. 소결온도 920˚C-960˚C, 소결시간 2시간일 때의 고주파 유전특성으로는 유전상수가 43.6, Qxfo값이 13,200 이상, τf =-14.36ppm/˚C을 얻었다.

YBa2Cu3O7-x결정입계 접합을 이용한 마이크로파 감지소자 YBa2Cu3O7-x초전도체 박막을 화학증착법을 이용하여 LaAIO3단결정 위에 증착하여 임계온도 90K이상 임계전류밀도 105/A cm2(77K) 이상의 우수한 박막을 제작하였다. 이를 포토작업과 이온밀링을 실시하여 수 마이크로미터 크기의 브릿지 형태로 만든 후 이들의 전류전압 특성을 조사하였다. 브릿지에 입사된 마이크로파의 크기에 따라 브릿지 간의 임계전류값의 저하가 관찰되었으며 동시에 샤피로스텝을 관찰할 수 있었다.

In this study, we evaluated the effect of the type of sewage sludge (digested, non digested) on drying efficiency according to the polymer injection rate. The drying characteristics were shown using a near-infrared ray (NIR) and a microwave. As a result of the drying characteristics with NIR at a polymer dose ratio of 8%, the heating up period is up to 6 minutes after the start of the drying experiment. Afterwards, the constant rate drying period of the digested sludge (A, C and G sites) was 6 minute → 18 minute, showing a rapid decrease in moisture. On the other hand, non digested sludge (B, D, E, F, H, I, J and K sites) showed gradual drying characteristics compared to digested sludge until complete drying (10%). As the polymer dose ratio of 10% and 12%, the heating up period for digested sludge is up to 6 minute after the start of the experiment. Afterwards, the constant rate drying period of the digested sludge was 6 minute → 20 minute, showing a rapid decrease in moisture. On the other hand, the heating up period of non digested sludge was up to 10 minute after the start of the experiment, and the constant rate drying period was 10 minute → 22 minute, which was shorter than digested sludge. As a result of the drying characteristics with microwave at a polymer dose ratio of 8%, 10% and 12%, the constant rate drying period the digested sludge was 4 minute → 20~22 minute, showing a rapid decrease in moisture. On the other hand, non digested sludge of the constant rate drying period was 4 minute → 22~30 minute, which was longer than digested sludge.

The purpose of this study was to determine the influence of microwave on the mechanical properties of epoxy mortar. The setting time, compressive strength and bond strength of epoxy mortar was investigated. The moisture content of the concrete substrate was taken into consideration to assess its effect on the bond between epoxy mortar and concrete. To verify the efficiency of concrete repair, flexural strength of repaired beams was measured. It was observed that microwave can effectively used to cure epoxy mortar and develop adequate strength in shorter time when compared to curing at room temperature.

The quality standards of solid refuse fuel (SRF) define the values for 12 physico-chemical properties, including moisture, lower heating value, and metal compounds, according to Article 20 of the Enforcement Rules of the Act on Resource Saving and Recycling Promotion. These parameters are evaluated via various SRF Quality Test Methods, but problems related to the heavy metal content have been observed in the microwave acid digestion method. Therefore, these methods and their applicability need improvement. In this study, the appropriate testing conditions were derived by varying the parameters of microwave acid digestion, such as microwave power and pre-treatment time. The pre-treatment of SRF as a function of the microwave power revealed an incomplete decomposition of the sample at 600 W, and the heavy metal content analysis was difficult to perform under 9 mL of nitric acid and 3 mL of hydrochloric acid. The experiments with the reference materials under nitric acid at 600 W lasted 30 minutes, and 1,000 W for 20 or 30 minutes were considered optimal conditions. The results confirmed that a mixture of SRF and an acid would take about 20 minutes to reach 180 oC, requiring at least 30 minutes of pre-treatment. The accuracy was within 30% of the standard deviation, with a precision of 70 ~ 130% of the heavy metal recovery rate. By applying these conditions to SRF, the results for each condition were not significantly different and the heavy metal standards for As, Pb, Cd, and Cr were satisfied.

Background : Bioactive substances, viscumneoside III and homoflavoyadorinin B, were isolated from korean mistletoe. Before, the isolated compounds were performed to identify the effect on tyrosinase inhibition activity. It is generally known that the biological activity of aglycon is better than the glycone attached to sugars in natural products. Methods and Results : In this study, the glycone of mistletoe were converted into homoeriodictyol and velutin, which are aglycon, respectively, by microwave irradiation, and their tyrosinase inhibitory activity was investigated. Experimental results showed that microwave irradiation mistletoe extracts showed superior tyrosinase inhibitory activity than untreated extracts. Conclusion : These results revealed that the whitening acivity of microwave irradiation Korean mistletoe can be utilized for the skin cosmetics.

The technology for sludge drying using a microwave is a primary process in producing solid refuse fuel in the waste-toresource process. In this paper, the drying efficiency is improved by investigating chamber types such as square and circle with various mechanical conditions such as the magnetron power, the height of microwave irradiation, and the sludge thickness. In identical conditions, the moisture content was generally uniform in the circle chamber due to the uniform distribution of microwave irradiation, and the drying efficiency was higher in the circle chamber compared to the square chamber. In the case of the circle chamber, the drying rate was increased by more than 30% and the energy for sludge drying 507.9 kcal/kg of water was reduced. Hence, the application of a circle chamber should save energy consumption in sludge drying.

Wood moisture content is the effect on carbonization properties of wood heated by microwave no greater, the effect on the thickness and density of the timber is determined to be greater. I.e. carbonization time and temperature regardless of the species in accordance with the water in the timber inside the heating with microwave is wood internal temperature is by the slow diffusion and the rate of evaporation of moisture trapped the thicker the thickness of the wood is increased thickness and density that is inversely proportional the feed.

최근 하수슬러지의 고형연료화와 관련하여 건조 기술에 대한 관심이 높아지고 있다. 현재 산업용 건조 기술에는 여러 가지가 있으나, 일반적으로 대류 열전달 방법인 열풍 건조가 많이 이용되고 있다. 그러나 열풍 건조는 유지 관리 비용이 크며, 외부 조건에 영향을 받는 등의 운전상 어려움이 있다. 이에 비해 마이크로파 건조는 복사에 의한 내부가열 방식으로 건조시간을 단축시킬 수 있으며, 에너지효율 면에서도 뛰어나다. 그러나 국내에서는 적용 실적 및 성공 사례의 부족으로 인해 활용되지 못하고 있는 실정이다. Batch type의 lab-scale 1 ~ 4kW급 마이크로파 건조기를 사용하였으며, 하수슬러지 건조 시 피건조물의 최적 투입 두께는 2 cm 이하, 마이크로파의 최적 조사 높이는 조사너비의 70%로 도출되었다. 건조효율 평가를 위하여 2.4 kW급 열풍 건조기를 이용하여 비교 실험을 진행한 결과, 열풍 건조에 비해 마이크로파 건조가 동일 조건 하에서 건조시간은 2.7배 단축되었으며, 수분증발효율은 4배 높은 것으로 나타났다. 특히 수분함량 60 ~ 10% 구간의 수분증발효율은 마이크로파가 열풍보다 약 6배 높은 것으로 나타났으며, 피건조물의 초기 수분함량이 낮을수록 마이크로파 건조가 더 유리한 것을 확인하였다.