The heavyweight industrial waste was used as concrete ingredient instead of natural aggregate, however, design standard did not consider effects of heavyweight aggregate on flexural strength. Therefore, in this paper, correlation between compressive and flexural strength of concrete using industrial was compared. From the results, compressive strength and flexural strength decreased with industrial waste increasing. And, it was shown that the test results of flexural strength were higher than the predicted value from design standard.

The purposes of this study is to evaluate the adhesion in flexure and adhesion in tension between old-plain cement mortar and new-polymer cement mortar that has been widely used as finishing and repairing materials of RC structures. From the test results, the adhesion in flexure and adhesion in tension of polymer-modified mortar to plain cement mortar are much higher than that of plain cement mortar, and are increased with increasing polymer-cement ratio. The maximum strengths show at polymer cement mortar using EVA dispersion, and those are about 1.69 and 2.10 times respectively, plain cement mortar.

In this study, the shear performance of the hollow slab was evaluated through experiments with the web width and volume fraction of steel fiber as variables. The lung pet bottles were used as a hollow materials. The results showed a performance difference of 19.4 to 52.3% depending on the web width, and a mixture of steel fibers showed a higher shear performance of 4.8 to 33.7%.

본 연구는 순환골재를 사용한 콘크리트의 활용증대 방안으로 철근콘크리트 구조물의 노후화와 내구성 저하 시 보수․보강으로 사용되는 FRP (AFRP, CFRP) 판으로 보강된 순환골재 고강도콘크리트(40MPa, 60MPa) 보를 제작하여 순환골재 철근콘크리트 보의 휨 보강에 대한 적용성을 평가하고자 한다 기존의 표면매입보강에 따른 에폭시와 FRP 판의 부착력을 고려하지 않기 위해 콘크리트 타설 전 FRP 보강판을 거푸집에 미리 설치하였으며, 순환골재 치환율(30%), 콘크리트 강도(40MPa, 60MPa), 이형철근(D10, D13), FRP 판의 종류(AFRP 판, CFRP 판)를 변수로 12개 실험체를 제작하여, FRP 판과 순환골재 치환율에 따른 휨 성능을 분석하였다. 그 결과 FRP 판으로 보강한 실험체는 무보강 실험체에 비해 최대 17% 증가하는 경향을 나타내었으며 AFRP 판에 비해 CFRP 판의 보강 성능이 우수한 것으로 나타났다. 또한 순환골재 치환율에 따른 보강 성능의 차이는 없는 것으로 나타났다. 실험에 의해 측정된 균열모멘트는 파괴계수를 이용한 결과 기준식과 비슷한 값을 나타났으며 휨 모멘트는 FRP 판을 보강한 일부 시험체가 KCI 2012와 ACI 440-2R에서 제시한 기준을 만족하지 못하는 것으로 나타났다.

High-rise buildings in recent years are increasing demand for high strength. However, the higher the floor, the greater the weight of the building, resulting in structural problems. In this study, the shear span ratio was equal to 1.5, and the effect of the web width (100 mm, 150 mm) on the shear strength of I-type flexural members was evaluated.

본 연구에서는 양생조건이 다른 압축강도 90 MPa 수준의 고강도 콘크리트 부재의 휨거동 실험을 수행하였다. 실험변수는 정상 및 저온 양생 조건, 인장 철근량 및 콘크리트 압축강도 수준 등을 고려하였다. 8개의 보 부재를 제작하여 휨 실험을 수행하였으며 균열 간격, 하중-처짐 관계, 하중-변형률 관계 및 연성지수를 파악하였다. 실험결과는 철근량이 증가함에 따라 균열 개수는 증가하고 균열간격은 감소하는 경향 을 나타내며, 콘크리트 강도가 높을수록 균열개수가 줄어들기는 하지만 그 효과는 철근량보다는 상당히 작은 것을 알 수 있었다. 설계기준에서 제안된 평균 균열 간격 식과 비교한 결과, 실험결과가 제안식의 결과보다 약간 크게 나타났으나, 제안식은 콘크리트 강도 및 양생조건을 반영 하지 못하는 문제점이 있다. 정상 양생된 부재들의 연성지수는 3.36~6.74이며, 저온 양생된 부재들의 연성지수는 1.51~2.82으로 나타나, 저온 양생된 부재들의 거동은 정상 양생된 부재들에 비해서 연성도지수가 저감됨을 확인하였으며, 본 연구와 기존 연구의 연성지수를 비교한 결과, 고강도 콘크리트 부재의 연성지수는 선행연구의 보통강도 콘크리트의 연성지수 보다 크게 나타났으나, 더 구체적인 결과를 파악하기 위해서 는 추가연구가 필요하다고 판단된다.

This paper describes the flexural characteristic of high strength steel fiber reinforced concrete (SFRC) prisms with different fiber tensile strength. All mixtures have specified compressive strength of 80 MPa and fiber volume fraction of 0.5% and 1.0%. In accordance with EN-14651, SFRC prisms were made and tested under bending loading. Test results indicated that steel fiber has no significant effects on compressive behavior of SFRC. However, flexural behavior of high strength SFRC was improved considerably with increase of fiber tensile strength.

The purpose of this study is determining the effects of flexural behavior of aramid fibers in ultra high performance concrete. The 10 kinds of aramid fibers with different length, diameter and twisting were used. The flexural behavior was determined by bending tests on specimens, which was prepared by mixing 1 % of volume fractions of aramid fibers into ultra high performance concrete mortar. Consequently, the load-displacement relationship curves were obtained by using the test results for each kinds of aramid. While the specimen that contains the small diameter of aramid fiber gives the strong flexural strength due to large contact area between the fiber and concrete matrix, that specimen by small diameter of aramid fiber does not guarantee the ductile behavior of specimen like the steel fiber. But the length and twisting of aramid fiber gives the ductile behavior of ultra high performance concrete flexural specimen.

The load-deflection curve and neutral axis changing curve, which were drawn by data from tests were analyzed. Both of steel fiber and reinforcing bar habe effect to induce the behavior of segmental U-shaped girder. The combination of 0.7% or 1.0% steel fiber and reinforcing bar sowed the effective ductle behavior of segmental U-shaped girder. The relationship of load-deflection and the crack pattern indicate that the appropriate combination are UFS1.0 and CFS1.0

This study is an analytical research on the size effect of concrete flexural-compressive strength. The meso-scale finite element method was used to analyze various sizes of specimens. As a result of the analysis, the size effect that the flexural-compressive strength becomes smaller as the size of specimen becomes bigger is analytically confirmed.

본 연구에서는 휨을 받는 압축강도 80 MPa 수준의 고강도 콘크리트 부재의 구조거동 실험 연구를 수행하였다. 실험변수는 보통(SD 400) 및 고강도(SD 600)철근, 0.98~1.58%의 종방향 철근비, 200×250, 200×300 mm의 단면크기를 고려하였다. 9개의 보 부재를 제작하여 휨 실 험을 수행하였으며 극한휨강도, 하중-처짐 관계, 균열 형태, 파괴형상 및 연성을 파악하였다. 실험결과는 철근비가 증가함에 따라 휨강도는 증 가하고 연성은 감소한다. 또한, 철근비가 증가함에 따라 균열의 개수가 증가하며 균열폭은 감소하는 경향을 나타내었다. 철근의 강도 등급에 따른 하중-균열폭 관계는 뚜렷한 차이를 나타내지 않는다. 콘크리트 비선형거동 해석을 수행하였으며, 극한하중 예측값과 측정값을 비교하였 다. 고강도 콘크리트의 휨거동 예측 결과는 실험부재의 휨강도를 전반적으로 과소평가하고 있다.

This paper examines the effect of steel fiber volume fraction on compressive and flexural properties of high-strength concrete with compressive strength of 40 MPa. The fiber volume fractions used in this study consist of 0.5, 0.75 and 1.0%. The prisms with 150x150x550 mm were made and tested in accordance with EN-14651.

이 연구에서는 순환굵은골재를 사용하여 31∼38 MPa 범주의 압축강도를 갖는 콘크리트의 보의 휨강도 실험연구를 수행하였다. 천 연굵은골재에 대한 순환굵은골재의 치환률과 철근비를 실험변수로 고려하였다. 순환굵은골재의 치환률로써 0, 30, 50 및 100%를 고려하였으 며, 주철근의 철근비로써 0.50, 0.79 및 1.14%를 고려하였다. 4점 하중재하 시험방법을 통하여 순환골재 콘크리트 보의 균열 및 파괴거동, 하중- 처짐 관계 특성을 파악하였다. 천연굵은골재 보와 순환굵은골재 보의 휨균열 형상은 거의 유사하며, 전반적으로 순환굵은골재 보의 균열간격 이 천연굵은골재 보의 균열간격보다 작다. 순환골재치환률에 따른 균열폭 크기는 뚜렷한 차이를 나타내지 않는다. 또한, 설계기준에 의한 예측 식을 이용하여 실험 부재의 휨강도를 산정하였다.현행 설계기준에 의한 순환골재 콘크리트 보의 휨강도 예측결과는 실제의 휨강도를 과소평 가하여 보수적인 설계를 제공하는 것으로 나타난다.

형상비(M/VD, shear span-depth ratio)가 4.5인 축소모형의 원형기둥 실험체 3개를 제작하였다. 철근콘크리트 기둥 실험체의 단면 은 원형이고 중공단면으로 제작되었다. 철근콘크리트 기둥 실험체의 단면 지름은 400 mm, 중공 지름은 200 mm이다. 일정한 축력 하에서 반복 하중을 가력하는 준정적 실험을 수행하였다. 실험체의 주요변수는 횡방향철근비이다. 모든 실험체의 횡방향 나선철근 체적비는 소성힌지 구 간에서 0.302~0.604%의 값을 갖는다. 이 값은 도로교설계기준에서 요구하는 최소 심부구속철근 요구량의 45.9~91.8%에 해당하며, 이는 내진 설계가 되지 않은 기존 교각이나 내진설계개념으로 설계되는 교각을 나타낸다. 본 연구의 최종목적은 실험적 기초자료의 제공과 함께 성능단 계별 균열거동, 하중-변위 이력곡선, 에너지 소산 능력, 등가점성감쇠비, 잔류변형, 유효강성 등 내진성능의 정량적 수치와 경향을 제공하기 위 한 것이다. 본 논문에서는 실험결과를 통해 분석된 실험변수에 따른 실험결과들을 공칭강도, 비선형 모멘트-곡률 해석 결과, AASHTO LRFD 및 도로교설계기준(한계상태설계법)과 같은 기준들과 비교하였다.

In this study, five high intelligent concrete (HIC) test specimens were fabricated by reinforcing the cement mortar with garnet, fiber (nylon and polypropylene), and shape memory alloy (SMA), to examine the effects of the numbers and positions of the reinforcements on the physical characteristic of the SMA. In improving the yield strength and structural self-rehabilitation capability, two or more hybrid fiber, PP and SMA reinforcements, as in SMA-PP, SMA-NP, SMA-2 yielded better results than SMA-1.

This paper describes the effects of tensile strength and aspect ratio of steel fiber on flexural behavior of high-strength SFRC notched beam. Test results indicated that flexural properties of SFRC improved with increasing in aspect ratio and tensile strength of steel fiber.

이 논문의 목적은 압축강도 130 MPa급의 고강도 강섬유 보강 콘크리트 보의 휨거동 특성을 파악하는데 있다. 부피비 1.0%의 강섬 유와 철근비 0.02 이하의 철근으로 보강된 고강도 강섬유 보강 콘크리트의 휨거동 특성 실험결과를 제시하였다. 일반강도철근과 고강도철근 을 실험 부재에 사용하였다. 강섬유 보강 콘크리트의 압축 및 인장거동 재료 실험과 모델링을 수행하였다. 강섬유 보강 콘크리트의 하중-균열 개구변위 실험결과를 반영하여 가상균열모델에 근거한 역해석을 통해 인장거동모델링을 제시하였다. 실험결과는 강섬유 보강 콘크리트와 고 강도철근의 사용은 균열제어 및 연성 거동에 유리한 것을 나타낸다. 일반강도철근을 사용한 보의 휨강도 실험값에 대한 수치해석에 의한 예측 값의 비는 0.81~1.42를 나타내고, 고강도철근을 사용한 보의 휨강도 실험값에 대한 수치해석에 의한 예측값의 비는 0.92~1.07을 나타낸다. 수 치해석에 의한 휨강도는 실험결과를 합리적으로 예측하고 있는 것으로 판단된다.

as subsea tunnel support. As a result, the shotcrete mixture with slag is excellent evaluated in terms of flexural strength compared with existing shotcrete.

The flexural capacity of concrete beams with high compressive strength of 80 MPa is described. This study aims to investigate the structural behavior of concrete beams such as crack patterns, failure mode, load-deflection relationship, moment-curvature relationship and strains in concrete.

본 논문에서는 UHPC 바닥판과 강재 거더를 이용하여 합성보를 구성할 때, UHPC 바닥판의 높은 강도와 강성으로 인하여 합성보 구성 시에 강재 거더의 상부 플랜지를 없앤 역T형 거더를 적용하고자 하였다. 그러나 현재까지 강재 복부에 설치되는 전단연결재에 대한 거동, 역T형 강거더 합성보의 휨거동 특성 등은 실험 및 이론적으로 평가된 적이 거의 없는 실정이다. 이를 위하여 UHPC 압축강도, 전단연결재 간격 및 바닥판 두께 등을 변수로 하는 역T형 거더와 UHPC바닥판 합성보 16개의 휨거동 실험결과를 근간으로 하여 실험결과와 UHPC의 인장연화 거동을 고려한 재료모델 해석결과를 비교하였다. 역해석에 의한 인장연화곡선에서 UHPC의 인장강도는 6.57 MPa(120MPa의 경우) 및 9.57 MPa(150MPa의 경우)를 나타내고 있으며, 전단연결재 간격이 좁을수록 실험결과와 해석결과가 명확하게 근접하는 겻으로 나타났으며, 바닥 판 두께가 두꺼우며 UHPC 압축강도가 작을수록 동일한 경향이나, 이 영향은 다소 작은 것으로 나타났다. 따라서 실험결과와 해석결과를 종합 적으로 비교하면, UHPC 합성보의 실험결과와 해석결과는 비교적 잘 일치하고 있으므로 재료 실험으로부터 산정된 인장연화곡선은 UHPC의 실제 거동을 합리적으로 반영한다고 판단된다.