Acrylonitrile–butadiene–styrene (ABS) terpolymer was compounded with short carbon fiber (CF) and carbon nanotube (CNT) using a micro-extruder followed by the injection molding process. Composite samples were fabricated with loading ratios of 20 wt.% CF and 0.1, 0.5 and 1.0 wt.% of CNT. Mechanical, electrical, thermo-mechanical, thermal, melt-flow, and structural investigations of ABS-based composites were conducted by performing tensile, impact, hardness, and wear tests, conductive atomic force microscopy (AFM), dynamic mechanical analysis (DMA), thermal gravimetric analysis (TGA), melt flow rate test (MFR), scanning electron microscopy (SEM) characterization techniques, respectively. According to mechanical test data of resultant composites including tensile and impact test findings, CNT additions led to the remarkable increase in tensile strength and impact resistance for CF reinforced ABS composites. The formation of synergy between CNT nanoparticles and CF was confirmed by electrical conduction results. The conductive path in ABS/CF composite system was achieved by the incorporation of CNT with different loading levels. SEM micrographs of composites proved that CNT nanoparticles exhibited homogeneous dispersion into ABS matrix for lower loadings.

국내 주요 사회기반시설의 70% 이상이 철근콘크리트 구조물로 구성되어 있다. 최근 다양한 사회적ㆍ환경적 변화로 인한 내하력 저하 및 노후화 진행이 발생됨에 따라 섬유강화 복합소재(FRP)를 활용한 유지보수 수요 및 비용이 급격히 증가되 고 있다. 이에 따라 보다 경제적이고 효율적으로 FRP 보강재를 활용함에 있어서 성능을 예측할 수 있는 방법이 요구된다. 본 연구에서는 CFRPㆍBFRP 복합재료를 실험 대상으로 선정하고 성능을 결정하는 주요 인자인 섬유/수지 함침률을 54.3%, 43.9%, 39% 3가지로 분류하여 성능을 평가하고 이를 활용하여 FRP의 성능을 예측할 수 있는 모델식을 개발하고자 하였다. 매개변수에 따른 성능평가 결과, 두 섬유 모두 함침률이 낮아질수록 재료성능 또한 감소되는 것이 확인되었으며, 특히 BFRP의 경우 39%의 함침률에서 감소폭이 CFRP 대비 더 큰 것으로 나타났다. 실험 결과와 기존의 예측 모델식과의 성능 비교를 통해 약 15%의 오 차가 나타나는 것을 확인하였으며, 이에 따른 보정계수를 산정하여 예측 모델식을 재정립하였다.

콘크리트 경화 시 발생하는 수분증발로 인한 건조수축은 콘크리트의 균열을 발생시킨다. 콘크리트에 발생하는 균열 은 콘크리트의 내구성을 저하하여 안정성과 사용성에 문제를 발생시킨다. 이러한 문제점을 보안하기 위해 콘크리트에 강섬유를 혼입하여 건조수축으로 인한 균열을 방지하는 강섬유 보강 콘크리트 (SFRC)에 관한 연구가 진행되고 있다. 강섬유는 콘크리트 의 균열단면에서 가교역할, 부착작용을 통해 건조수축으로 인한 균열발생을 억제하고 균열 폭을 감소시키는 효과가 있다. 본 논 문에서는 강섬유의 인장강도에 따른 강섬유 보강 콘크리트의 건조수축 제어성능을 평가하였다. 자유건조수축 실험과 구속건조 수축 실험을 진행하였으며 실험 결과를 콘크리트의 인장응력으로 변환하여 콘크리트 직접인장실험 결과와 비교하였다. 강섬유 의 자유건조수축 저감 효과는 미미하지만 강섬유의 인장강도가 증가할수록 구속건조수축으로 인한 균열제어에 효과적임을 확인 하였다. 또한 강섬유의 인장강도가 증가할수록 콘크리트의 인장응력이 증가함을 확인하였다.

In this present investigation, machinability studies on novel aluminum composite with hybrid reinforcements of copper-coated 4% carbon fibers (CFs) and 3% nanoclay in AA6026 matrix fabricated by compocasting method is performed. Step drill bit and multifaceted drill bit are used by adopting central composite design (CCD) in response surface methodology (RSM). The outcomes show that, with a rise in rotational speed surface irregularities, resultant force and material removal rate (MRR) intensifies, and with the additional rise in rotational speed, all the outputs decrease considerably. High MRR, resultant cutting force, and surface roughness are obtained with multifaceted carbide drills, compared with a step drill. Desirability function is used to maximize the MRR and minimize the resultant cutting forces considering the constant surface roughness of 3 μm. The optimal values are rotational speed of 1285 rpm, feed rate of 60 mm/min with the step drill bit, producing an MRR of 0.0439 kg/sec and a resultant cutting force of 185.818 N. The second-order empirical models are developed for outputs, which are fed into the non-traditional metaheuristic Evaporation Rate-based Water Cycle Algorithm (ER-WCA) therefore the lower objective value is achieved with step drill of 51.7421. It is found that using a step drill the machinability performance of this hybrid nanocomposite is well improved than the machining with other drill bits. This composite fulfills the norms of 2000/53/CE-ELV European environmental directives.

필로티 공간은 일반적인 건축부재와 달리 부재가 외기와 접해 있고 실내에서 발생 가능한 화재와 가연물의 종류 및 배치 등이 달라 다양한 화재의 위험으로부터 노출되어 있다. 필로티 구조는 기둥으로만 이루어진 사방이 트인 구조로 인해 화 재가 발생할 경우 화재피해를 입은 기둥은 강도 및 강성이 저감되고 부재의 저항성이 저하되므로 단시간 안에 온도가 상승하여 구조체에 영향을 미친다. 이러한 문제점이 발생한다면 건축물 파손으로 인해 피난로를 차단당하여 많은 인명피해가 일어날 것 으로 사료된다. 본 연구에서는 다가구주택의 필로티 공간에서 화재 발생으로 인해 철근콘크리트 기둥에 미치는 화재영향을 확 인하고자, 기둥 국부화재실험을 통해 보강재에 따른 RC 기둥의 온도분포 및 파괴양상을 검토하였다.

Carbon fiber and its composites are increasingly used in many fields including defence, military, and allied industries. Also, surface quality is given due importance, as mating parts are used in machineries for their functioning. In this work, the turning process is considered for Carbon Fiber Reinforced Polymer (CFRP) composites by varying three important cutting variables: cutting speed, feed, and depth of cut. Correspondingly, the surface roughness is measured after the completion of turning operation. As well, a prediction model is created using different fuzzy logic membership function and Levenberg–Marquardt algorithm (LMA) in artificial intelligence. Later, the surface roughness values from the developed models are compared against the experimental values for its correlation and effectiveness in using different membership functions of fuzzy logic and ANN. Thus, the experimental results are analyzed using the effect graphs and it is presented in detail.

Polyacrylonitrile (PAN)-based carbon fibers (CFs) and their composites, CF-reinforced plastics, have garnered significant interest as promising structural materials owing to their excellent properties and lightweight. Therefore, various processing technologies for fabricating these advanced materials using thermal energy have been intensively investigated and developed. In most cases, these thermal energy-based processes (heat treatment) are energy and time consuming due to the inefficient energy transfer from the source to materials. Meanwhile, advanced processing technologies that directly transfer energy to materials, such as radiation processing, have been developed and applied in several industrial sectors since the 1960s. Herein, general aspects of radiation processing and several key parameters for electron-beam (e-beam) processing are introduced, followed by a review of our previous studies pertaining to the preparation of low-cost CFs using specific and textile-grade PAN fibers and improvements in the mechanical and thermal properties of CF-reinforced thermoplastics afforded by e-beam irradiation. Radiation processing using e-beam irradiation is anticipated to be a promising method for fabricating advanced carbon materials and their composites.

이 연구는 바잘트 섬유시트로 전단보강한 철근콘크리트 보의 전단경간비에 따른 구조물의 구조적 거동을 실험을 통해 확인하였다. 철근콘크리트 보의 전단보강은 무보강, 45도, 90도, U형보강을 변수로 두었으며 전단경간비에 따른 실험결과 U형으로 보강하였을 때 철근콘크리트 보의 전단보강효과가 높음을 확인하였다.

Cu matrix composites reinforced with chopped carbon fiber (CF), which is cost effective and can be well dispersed, are fabricated using electroless plating and hot pressing, and the effects of content and alignment of CF on the thermal properties of CF/Cu composites are studied. Thermal conductivity of CF/Cu composite increases with CF content in the in-plane direction, but it decreases above 10% CF; this is due to reduction of thermal diffusivity related with phonon scattering by agglomeration of CF. The coefficient of thermal expansion decreases in the in-plane direction and increases in the through-plane direction as the CF content increases. This is because the coefficient of thermal expansion of the long axis of CF is smaller than that of the Cu matrix, and the coefficient of thermal expansion of its short axis is larger than that of the Cu matrix. The thermal conductivity is greatly influenced by the agglomeration of CF in the CF/Cu composite, whereas the coefficient of thermal expansion is more influenced by the alignment of CF than the aggregation of CF.

이 연구는 탄소섬유시트의 보강겹수와 보강위치에 따른 I형 PFRP 휨부재의 휨보강 효과에 대해 조사하였다. 또한, 탄소섬유시트로 보강한 PFRP 휨부재의 실험적, 이론적으로 확인하기 위해 유한요소해석을 실시하였으며, 휨실험 결과와 이론적 해석결과를 비교분석하였다. 휨실험 결과와 유한요소해석 결과는 이론적인 결과와 비교한 결과 일치하는 경향을 보였고, 휨보강 효과가 큰 탄소섬유시트 2겹을 보강한 시편에서 결과에서 오차가 가장 크게 발생하였다.

취성특성을 가진 탄소섬유복합체의 인장특성을 결정하기 위해 ASTM D 3 0 39에 따라 인장시험을 실시하였다. 극한시 점에 박리, 부분파단으로 인해 스트레인 게이지의 계측값의 변동성이 커져 신뢰성을 확보하기 어렵기 때문에 극한응력과 탄성 계수를 이용한 유효극한변형률을 제안하고, 극한계측변형률과 상호보완하였다. 특히 게이지가 비정상적으로 작용할 경우에도 적용이 가능하다는 장점이 있다. 또한 유효극한변형률을 결정하는 탄성계수는 단일시편에서 여러 변형률 구간에 대하여 평가하여 비교 검증할 수 있다.

이 연구는 탄소섬유시트의 보강겹수에 따른 I형 PFRP 휨부재의 휨보강 효과를 조사하기 위해 길이 600mm의 PFRP 휨부재와 상하부 플랜지에 1mm 두께의 탄소섬유시트로 보강하여 휨실험을 수행하였다. 또한, 탄소섬유시트의 보강겹수와 보강 위치에 따른 I형 PFRP 휨부재의 휨보강 효과와 단면 감소량에 대해 조사하였다. 그 결과 2겹으로 보강하였을 때 휨강도와 휨강성이 증가함을 확인하였다.

본 연구에서는 섬유보강콘크리트(SFRC) 구조물의 수치해석을 위한 K&C모델의 보정기법을 소개하였다. SFRC 1축 및 3축 압축강도 실험결과를 기반으로 보정을 수행하였으며, 단일요소 해석결과를 실험결과와 비교함으로써 보정 기법의 검증을 수행하였다. 또 한, 변형률 속도의 영향을 반형하기 위해 동적증가계수(DIF)를 고려하여 SFRC 구조물의 발사체 관통해석을 수행함으로써 보정기법의 적용 가능성을 확인하였다.