This paper is focused on flexural bahavior of cement composites reinforced with carbon fibers as a part of research for improving a seismic performance of structures using carbon fiber reinforced concrete(CRFC). Flexural behavior test was conducted on respective specimens reinforced with different fiber length(6mm, 12mm) and contents(0%, 0.5%, 1.0%, 2.0%, 3.0%). The result of the test showed that the flexural performance of carbon fiber reinforced cement composites are directly proportional to the fiber contents except for the specimen reinforced with 3% carbon fiber.

Due to the enlargement and high-rise of reinforced concrete structure, the application of high functional material is required. However, high-strength bar is recently introduced to the country and the material is insufficient to measure the variation of quantity of rebar quantitatively when using high-strength bar. For these reasons, this study is to provide useful data in cost decision making when applying high-strength bar at a stage of architectural project planning. For residence-commerce complex buildings, we set up six types of conditions such as in case of using only rebar, in case of using only high-strength bar, in case of using rebar mixed with high-strength bar and so on. With the standard of study model 1 that applies only SD400 regardless of rebar diameter, the analyzed result of rebar variation and the cost change of construction in other study model is as follows. When the rebar amount and cost in study model I was 100%, each ratio was 88.3% and 90.5% in study model II, 80.2% and 83.4% in study model III, 91.9% and 93.5% in study model IV, 88.9% and 87.7% in study model V and 82.4% and 85.5% in study model VI. Therefore, in case of rebar amount and construction cost, study model III was evaluated as the best that was applied only SD600.

KCI 2012 and ACI318-11 contains development length provisions for the use of headed deformed bars in tension and does not allow their tension lap splices. In ACI318-11, the confinement factor, such as transverse reinforcement factor, is not used to calculate the development length of headed bars. The purpose of this experimental study is to evaluate the effect of confinement details to the lap splice performance of headed deformed reinforcing bars in grade SD400 and SD500. The confinement details are stirrups and tie-down bars in lap zone. Test results showed that specimens with only stirrups had the brittle failure and could not increase lap strengths, and that specimens with composite confinements by stirrups and tie-down bars had the flexural strengths over than nominal flexural strengths. Stirrups with tie-down bars can have an effect on improvement in lap splice of headed bars in grade SD400 and SD500.

본 연구에서는 섬유종류에 따른 인발특성과 섬유보강 콘크리트의 휨특성에 대하여 평가하기 위하여, 섬유의 재질 및 형상 다른 후크형강섬유, 비정질 강섬유 및 폴리아미드 섬유에 대하여 인발시험과 섬유보강 콘크리트 시험체를 제작하여 휨특성을 평가하였다. 그 결과, 후크형 강섬유의 경우 최대인발하중에서 섬유가 매트릭스로부터 인발되었지만, 비정질 강섬유는 섬유와 매트릭스의 부착강도가 섬유자체의인장강도보다 높아 섬유가 매트릭스로부터 인발되지 않고 파괴되는 현상을 나타내었다, 한편, 폴리아미드 섬유는 연신율에 의해 최대인발하중까지 변위가 크게 발생하였으며, 최대하중이후에 섬유가 끊어지는 파괴특성을 나타내었다. 섬유보강 콘크리트의 휨특성에 있어서 비정질 강섬유는 매트릭스와의 부착강도가 높고, 섬유의 혼입개체수가 많아 콘크리트의 최대휨강도는 높았지만, 균열발생 이후 섬유가 매트릭스로부터 인발되지 않고 섬유가 파괴되는 것에 의해 응력의 저하가 급격하게 발생하지만, 후크형 강섬유보강 콘크리트는 균열발생 이후 섬유가 인발되면서 응력의 저하가 완만하게 발생하였다. 폴리아미드 섬유보강 콘크리트는 균열발생이후 섬유의 연신률에 의해 응력이 급격하게 저하하는 구간이 발생하였으며, 섬유와 매트릭스의 부착에 의해 재상승하였다가 섬유가 끊어지면서 파괴되었다. 섬유와 매트릭스의 인발특성은 섬유보강 콘크리트의 휨강도 및 변형 능력에 큰 영향을 미치는 것으로 판단된다.