PURPOSES : This study analyzes the service life of the repair methods of jointed plain concrete pavement (JPCP) on expressways in Korea using PMS data. METHODS : The Korea Expressway Corporation PMS data acquired from five major expressways in Korea were used for the analysis. The service lives of the repair methods were considered for two different cases: 1) the previous repair methods had been completely rerepaired by another or the same method due to their damage, and 2) the current repair methods were still in use. RESULTS : The service lives of D/G and section repair were shown to be at least 30 % and 50 % shorter than expected, respectively. Joint sealing and crack sealing exhibited a service life similar to that expected. The Mill-and-Asphalt-overlay method showed an approximately 30 % longer service life; this might be because some damage to the asphalt overlay is typically neglected until subsequent maintenance and repair. When multiple repairs were applied in series for an identical pavement section, the service life of repairs on previously damaged secti ons become even shorter compared to their first application. CONCLUSIONS : It was found that the analyzed service life of most important repair methods did not reach the expected service life, and that the service life of the same repair method becomes shorter as applied to the previously repaired concrete pavement sections. These shorter service lives should be seriously considered in future JPCP repair strategy development.

PURPOSES : The type and degree of structural conditions and influencing factors distributed across representative sections should be similar to those distributed across entire sections as the representative sections have been predominantly used for developing performance prediction models, which substitute entire sections of road pavement. Therefore, a logic that selects the representative sections with similar distributions of structural conditions and the influencing factors with those of entire expressway asphalt pavement sections requires development. METHODS : The logic developed in this study to select the representative sections of asphalt pavements comprised three steps. First, the data on the structural conditions of the pavement and the influencing climate conditions and pavement materials were collected and organized. Consequently, in the second step, the candidate sections were selected, with the severity of the structural conditions of the pavement distributed widely and evenly. Finally, in addition to the widely and evenly distributed pavement conditions, the representative sections with climatic conditions and pavement materials were selected. RESULTS : A total of 6,352 ordinary asphalt pavement sections and 596 composite asphalt pavement sections were selected as entire expressway asphalt pavement sections and the data were collected and organized according to the logic developed in this study. Three times the representation sections were selected as candidate sections and, finally, 85 sections were selected as representative sections. The distribution of structural conditions and influencing climate conditions and pavement materials in the representative sections were similar to those in the entire sections. In addition, the representative sections were spread evenly across the country. CONCLUSIONS : The sections presenting similar distributions of structural conditions and the influencing factors of entire expressway asphalt pavement sections could be selected in this study. Using the representative sections selected in this study, a remodeling index model will be developed for predicting the asphalt pavement sections that require large-scale repair.

본 논문은 증기이송튜브를 이용한 현장경화 보강튜브 삽입공법(Cured in placed pipe, CIPP)의 성능을 평가하기 위한 실험적 연구이다. 연구를 위해 증기이송튜브를 이용하여 CIPP 라이너 시편 및 CIPP 라이너로 보수된 콘크리트관 실험체를 제작 하였다. CIPP 라이너 시편을 이용하여 단ㆍ장기 휨특성을 평가하였으며, 단기 휨특성 시험변수로 시점으로부터 떨어진 거리를 고려하였다. 단기 휨거동 평가결과 CIPP 라이너의 휨강도 및 휨탄성계수는 ASTM 기준에서 제시하고 있는 휨강도 및 휨탄성계수의 197%, 154% 수준으로 우수한 단기 구조 성능을 보이는 것으로 나타났다. 또한 시점부로부터 떨어진 거리와 CIPP 라이너의 단기 휨특성은 큰 상관관계가 없는 것으로 나타났다. 장기 휨거동 시험내용을 이용하여 1차원 회귀분석을 실시한 결과 50년 경과 후 CIPP 라이너의 휨 탄성계수는 초기 휨탄성계수의 87.8%로 우수한 장기 구조 성능이 나타났다. 이 후 CIPP 라이너로 보수된 콘크리트관 실험체의 외압강도시험을 실시하였다. 외압강도시험 변수로 보수 유ㆍ무 및 시점으로부터 떨어진 거리를 고려 하였다. CIPP 라이너로 보수된 콘크리트관의 외압강도는 보수되지 않은 콘크리트관에 비해 초기균열 하중은 16.8%, 최대하중은 7.7% 증가한 것으로 나타났다. 외압강도 시험결과 시점으로부터 떨어진 거리와 외압강도는 상관관계가 없는 것으로 나타났다. 이는 실험체 제작시 증기이송튜브를 이용하여 CIPP 내부 모든 구간에서 균일한 경화온도를 확보할 수 있었기 때문으로 판단된다.

This paper sought to examine characteristics and differences of the construction methods and the materials of the wall repair by three command through individual command records and national documents. This paper is based on the management section of three commands(Samgunyoung), which was in charge of a repair and management of Hanyangdoseong(Seoul city wall) in 18th century. The purpose and background of the study are as follows. First, through each inscribed stones on the rampart and the parapet, it is to grasp accurately the point of change of Hanyangdoseng after the 18th century. Second, through inscribed stones, the site evidence of the repair work in the late Joseon Dynasty, it is to find out the aspects of the development process of repair and reconstruction technology of Hanyangdoseng.

The purpose of this study is to reveal the development process of modern repair systems in the Korean peninsula. Sasungjeon, one of the main buildings of Jangansa temple located in Geumgangsan, was repaired from 1941 to 1944. It was the very last restoration work of historic wooden architecture performed during the Japanese colonial era. This work was delayed multiple times because of insufficient materials and human resources. The Bureau of Education(學務局), which was in charge of repair work, understood that the problems of the repair system and suggested reorganizing the system as a solution. This study examined the repair work of Sasungjeon as a background of the bureau’s suggestion and considered this suggestion as an attempt to transform the repair system.

The purpose of this study was to analyze the correlation between conservation activities and the development of tourism in the modern period in the Korean peninsula. The main building of Jangansa Temple, located in Mt. Geumgang, was repaired in the 1930s. During the repairs, the Japanese General-Government actively engaged in the development of Mt. Geumgang and raised funds for the operation of the Korean Peninsula through tourism revenue. The repair work was carried out under the influence of the Mt. Geumgang development project. And its influence is revealed by reviewing official documents recording repair work. This study tried to clarify the relationship between development and repair work through official documents.

최근 국내에서 토목 및 건축구조물의 노후화 및 성능저하에 따른 사회적인 우려가 발생하고 있다. 일반적으로 노후 구조물의 보수보강 방법으로는 외부 부착공법이 가장 많이 사용되고 있으며 시공 용이성을 위하여 GFRP나 CFRP Sheet나 Plate를 활용한 부착 보강방법이 활발히 적용되고 있다. 그러나 이들 방법은 온도에 취약하며 탄소섬유의 경우 경제성이 낮다는 우려가 발생한다. 본 연구에서는 친환경적이고 내열성이 상대적으로 우수한 현무암 섬유(BFRP)를 활용하여 온도변화 및 콘크리트 표면 내 균열발생에 따른 BFRP-콘크리트의 인장 부착성능 및 파괴 패턴을 실험적으로 평가하였다. 그 결과 구조물의 온도가 상승함에 따라 BFRP-콘크리트 계면의 부착성능은 약 30%정도 감소하는 것으로 나타났으며 내열성 수지를 사용한 보강재의 경우 일반 함침용 에폭시 수지보다 부착성능이 다소 우수한 것으로 평가되었다. 콘크리트 표면 내 균열 발생된 경우 균열의 폭이 증가함에 따라 부착 성능은 약 20%씩 감소하는 것으로 나타났다. 하지만 균열보수제로 보강 후 계면에서의 부착성능의 경우, 보강 전 대비 약 30% 정도의 개선효과를 나타내었다.

PURPOSES: This study aims to evaluate the resistance to chemical attack of combined organic and inorganic hybrid mortars as the repair materials (i.e., HRM mortar) used for concrete road facilities through a comparison with mortars made from cement repair materials (i.e., IRM mortar). METHODS: Inorganic materials used as a binder and two mineral fillers were adopted to produce HRM mortars. The ratio of the main resin versus the hardener was fixed at 2:1. For comparison, IRM mortars made of cement repair materials were also manufactured. The mortars were exposed to chemical solutions, such as NaCl, MgSO4, Na2SO4, and H2SO4, with the same concentration of 5% after 7 days of curing. The compressive strength, compressive strength loss, mass ratio, and relative bulk density of the mortar samples exposed to the chemical solutions were measured at predetermined periods. In addition, a scanning electron microscope observation was performed to evaluate the microstructures and the products formed by the chemical reaction of the mortar samples. RESULTS : As a result, the resistance to chemical attack of the HRM mortars was found to be much better than that of the IRM mortars, regardless of the types of attacking sources. This finding implies that HRM is a highly promising and versatile material because of its excellent resistance to chemical attack. CONCLUSIONS: The application of the combined organic and inorganic hybrid mortars is a possible option for repair of concrete road facilities exposed to aggressive environments.

PURPOSES: The objective of this study is to evaluate the durable performance of combined organic and inorganic hybrid mortar as repair material (HRM mortar) for concrete road facilities via comparison with that of cement repair materials (IRM mortar). METHODS : To produce HRM mortars, inorganic materials as binder and 2 mineral fillers were adopted. The ratio of main resin versus hardener was fixed at 1:2. For comparison, IRM mortars made with cement repair materials were also manufactured. Compressive, flexural, and bonding strengths were measured at predetermined periods. For durability assessment, the scaling resistance, freezing & thawing resistance, rapid chloride penetration resistance, and acid attack resistance of those mortars were experimentally monitored. RESULTS: The durability performances of HRM mortars, especially with respect to freezing & thawing, rapid chloride penetration and acid attack, were identified to be much better than those of IRM mortars. This result implies that HRM is a highly promising and versatile material because of its excellent durability. CONCLUSIONS: It is concluded that the application of the combined organic and inorganic hybrid mortars is possibly an option for the repair of concrete road facilities exposed to aggressive environments.