This study was conducted to figure out the productivity of Italian ryegrass(IRG) and leaching water characteristics based on horse manure compost level in Jeju. This study was conducted for about six months. Six treatments were established : non-fertilizer(NF), chemical fertilizer 100%(CF), horse manure compost 50% and chemical fertilizer 50% combination(Combination), horse manure compost with 50% of nitrogen (50%), 100% of nitrogen(100%), 150% of nitrogen(150%). The highest amount of dry matter yield of IRG was revealed in CF(11,965± 564 kg/ha), and both 150% and Combination were second(p<0.05). Nitrate leaching tended to increase until the third analysis and then decreased. There were not significantly differences among mean nitrate concentrations. The findings of the study suggest that horse manure compost with 50% of nitrogen be applied for IRG as basal fertilization and then 50% of chemical fertilizer be applied as top fertilization.

Currently, the Korea Atomic Energy Research Institute (KAERI) is planning to build the Ki-Jang Research Reactor (KJRR) in Ki-Jang, Busan. It is important to safely dispose of low-level radioactive waste from the operation of the reactor. The most efficient way to treat radioactive waste is cement solidification. For a radioactive waste disposal facility, cement solidification is performed based on specific waste acceptance criteria such as compressive strength, free-standing water, immersion and leaching tests. Above all, the leaching test is important to final disposal. The leakage of radioactive waste such as 137Cs causes not only regional problems but also serious global ones. The cement solidification method is simple, and cheaper than other solidification methods, but has a lower leaching resistance. Thus, this study was focused on the development of cement solidification for an enhancement of cesium leaching resistance. We used Zeolite and Loess to improve the cesium leaching resistance of KJRR cement solidification containing simulated KJRR liquid waste. Based on an SEM-EDS spectrum analysis, we confirmed that Zeolite and Loess successfully isolated KJRR cement solidification. A leaching test was carried out according to the ANS 16.1 test method. The ANS 16.1 test is performed to analyze cesium ion concentration in leachate of KJRR cement for 90 days. Thus, a leaching test was carried out using simulated KJRR liquid waste containing 3000 mg·L-1 of cesium for 90 days. KJRR cement solidification with Zeolite and Loess led to cesium leaching resistance values that were 27.90% and 21.08% higher than the control values. In addition, in several tests such as free-standing water, compressive strength, immersion, and leaching tests, all KJRR cement solidification met the waste acceptance or satisfied the waste acceptance criteria for final disposal.

There has been much interest in recycling electronic wastes in order to mitigate environmental problems and to recover the large amount of constituent metals. Silver recovery from electronic waste is extensively studied because of environmental and economic benefits and the use of silver in fabricating nanodevices. Hydrometallurgical processing is often used for silver recovery because it has the advantages of low cost and ease of control. Research on synthesis recovered silver into nanoparticles is needed for application to transistors and solar cells. In this study, silver is selectively recovered from the by-product of electrodes. Silver precursors are prepared using the dissolution characteristics of the leaching solution. In the liquid reduction process, silver nanoparticles are synthesized under various surfactant conditions and then analyzed. The purity of the recovered silver is 99.24%, and the average particle size of the silver nanoparticles is 68 nm.

Phosphorus is an essential and irreplaceable element for all living organisms and its resource is limited. Significant amount of used phosphorus is collected in sewage treatment plant as sludge. Sludge ash after incineration contains about 10% of phosphorus in dry mass basis, which is comparable to phosphate rocks, and it is an important source of phosphorus recovery. Acid and alkali were used to leach phosphorus from sludge ash and compared for their leaching kinetics and performance. Phosphorus leaching by NaOH was fast and 0.2 N and 2 N NaOH leached 49% and 56% of the total phosphorus in the sludge ash at the L/S ratio of 100. Phosphorus leaching by sulphuric acid and hydrochloric were very fast and most of the phosphorus was leached in 5 minutes. In case of sulphuric acid 95% of the total phosphorus in the sludge ash was leached by 0.2 N at the L/S ratio of 100 and 93% was leached by 1 N at the L/S ratio of 10. 1 N hydrochloric acid leached 99% of the total phosphorus at the L/S ratio of 10. The results showed acids were more effective than alkali for phosphorus leaching from sludge ash and hydrochloric acid leached more phosphorus than sulphuric acid.

This study focuses on the development of an alkaline leaching hydrometallurgy process for the recovery of tungsten from WC/Co hardmetal sludge, and an examination of the effect of the process parameters on tungsten recovery. The alkaline leaching hydrometallurgy process has four stages, i.e., oxidation of the sludge, leaching of tungsten by NaOH, refinement of the leaching solution, and precipitation of tungsten. The WC/Co hardmetal sludge oxide consists of WO3 and CoWO4. The leaching of tungsten is most affected by the leaching temperature, followed by the NaOH concentration and the leaching time. About 99% of tungsten in the WC/Co hardmetal sludge is leached at temperatures above 90oC and a NaOH concentration above 15%. For refinement of the leaching solution, pH control of the solution using HCl is more effective than the addition of Na2S·9H2O. The tungsten is precipitated as high-purity H2WO4·H2O by pH control using HCl. With decreasing pH of the solution, the tungsten recovery rate increases and then decrease. About 93% of tungsten in the WC/Co hardmetal sludge is recovered by the alkaline leaching hydrometallurgy process.

We developed leaching kinetics models and a convective mass transfer model for water soluble solid in jujube (Zizyphus jujube) fruits with hot water. Hot-water leaching process was conducted at 90°C for 100 min. The ratio of solvent (volume, mL) to solid (mass, g) was set to varied ratios of 1:6, 1:8, 1:10, and 1:12.5. The mass transfer coefficients (k) were determined based on the 1st- and 2nd-order kinetic models. The amount of solvent influenced the extraction rate and yield. A higher extraction rate and a higher yield were obtained from a lower solvent to solute ratio (1:6, 1:8, 1:10) compared to high ratio (1:12.5). This implies that an appropriate amount of solvent (i.e., water) is necessary to conduct the extraction process of jujube fruit.

스캐폴드는 손상된 조직을 보호, 지지하고, 세포분화 및 증식을 위한 공간을 임시로 제공하여 조직의 회복을 유도한다. 이에, 스캐폴드막은 생체친화성과 생분해성을을 지녀야 한다. 본 연구에서는 Poly(L-lactide)를 사용하였고, 상전이법을 기초로 하여 스캐폴드막을 제조하였으며, 대형공극을 형성하기 위하여 염 침출법을 복합하여 사용하였다. 그 결과 높은 공극률의 다공성 스캐폴드막을 얻을 수 있었으며, 기존의 여타 방식에 비해 월등히 간단한 방식으로 스캐폴드를 제조할 수 있다는 결론을 얻을 수 있었다.

조직공학이란 손상된 조직에 대한 대체재를 개발, 제조하는 분야이며, 기증자로부터의 조직을 직접 이식하는 방법이 가장 널리 사용되어 왔으나, 최근에는 함성소재로부터의 캐폴드막 제조에 대한 연구가 진행되고 있다. 스캐폴드막은 공극률, 공극직경 및 공극간의 높은 연결성이 요구된다. 이에 대하여 용융주조에 이은 염 침출법이 알려져 있다. 본 연구에서는 용매주조에 이은 염 침출법을 사용하였으며, 이를 통하여 높은 공극률과 공극간의 연결성은 물룬 적합한 공극직경의 우수한 스캐폴드막을 제조하였다.