Multiwall carbon nanotubes (MWCNT) with two different (L/D) aspect ratios (7±2 μm/140±30 nm and 0.5–2 μm/8–15 nm) were surface treated using nitric acid (HNO3) and polyethyleneimine (PEI) prior to their deposition on carbon fibers (CF). Before the hierarchical reinforcement with CF-MWCNT, the CFs were treated with 3-glycidoxypropyltrimethoxysilane, a coupling agent (Z6040) and with poly(amidoamine) (PAMAM) a dendrimer containing an ethylenediamine core and amine surface groups. The MWCNT were deposited on the CF using two methods, by electrostatic attraction and by chemical reactions. The changes in the CF surface morphology after the MWCNT deposition were analyzed using SEM, which revealed a higher density and uniform coverage for the PAMAM-treated CF and the short MWCNTs. The interfacial adhesion of the composite materials was evaluated using the single fiber fragmentation technique. The results indicated an improvement in the interfacial shear strength with the addition of the short-MWCNTs treated with acid solutions and grafted onto the surface of the CF fiber using electrostatic attraction.

PVA 부직포의 방염성을 향상시키기 위하여 POCl3로 방염처리하였다. POCl3로 처리한 PVA 부직포의 물리적 및 열적 특성을 측정하고 분석하였다. 개질한 PVA 부직포는 대부분 물에 용해하지 않았으나 수축과 스웰링 특성을 보 였다. POCl3로 방염처리한 PVA 부직포의 열적 특성이 우수하고 방염특성이 원시료 보다 많이 우수한 것을 확인하였다. 그라프트 비와 염색성 사이의 선형관계는 PVA 부직포의 히드록시기와 POCl3가 공유결합으로 연결된 것에 기인하는 것 으로 분석되었다.

백색을 띄고 물리적·화학적으로 안정한 지르코니아는 열전도도가 낮고 강도와 인성, 내식성이 우수하여 단열재, 내화물과 같은 고온 재료와 각종 산업용 구조세라믹스에 사용되고 있다. 이러한 지르 코니아를 낮은 경도 및 굴절률 등과 같은 단점을 가진 고분자 코팅제에 도입하게 되면 화학적, 전기적, 광학적인 특성이 향상된다. 이와 같이 유기 소재에 무기 소재를 혼합하여 사용하는 유-무기 하이브리드 코팅을 목적으로 본 연구에서는 지르코니아 표면에 trimethylchlorosilane(TMCS)과 hexamethyldisilazane(HMDZ)을 사용하여 실릴화반응을 통한 -CH3기를 도입하여 소수성을 나노지르코 니아 표면에 도입하였다. 소수화된 지르코니아 표면에서의 TMCS와 HMDZ에 의해 도입된 Si-CH3의 존재는 FT-IR ATR spectroscopy를 통해 확인하였고, silicon 원소의 존재를 FE-SEM/EDS와 ICP-AES 를 통해 확인하였다. 또한, 개질 전후의 지르코니아를 아크릴레이트 단량체에 분산하여 침강속도를 확인 하여 분산성이 향상되는 것을 확인하였다. 지르코니아 입자의 크기 및 분포는 입도 분석기를 통해 확인 하였으며, BET 분석을 통해 개질 반응 전후의 비표면적은 18 m2/g 정도로 큰 변화가 없었다.

CE RCD (Recreational Craft Directive) is a certification for the design and construction of small vessels, including pleasure yachts, which are widely used not only in the countries within the European Union, but also in Japan and Southeast Asia. Recently, South Korean leisure craft shipyards have developed interest in exporting to foreign leisure craft markets such as Europe; however, they have encountered difficulties because of the CE RCD regulations, which are relatively complex and difficult to understand. The requirements for buoyancy and stability, which are essential properties that must be understood within the early stage of ship design, are defined based on ISO 12217. However, preparing this assessment according to ship classification regulations is an exceedingly complex task, even with knowledge of naval architecture. In this research, we have developed design support tools to systematically support assessments and preemptively define design information so that buoyancy and stability assessments based on ISO 12217 can be systematically prepared. Our research results were applied to actual examples of yacht design to confirm validity. We believe that the improved yacht design process presented in this research can act as a foundational reference for enhancing the effectiveness and systematic buoyancy and stability assessments.

The purpose of earthquake resistant design for typical bridges is the ‘No Collapse Design’ allowing emergency vehicles just after earthquakes. The Roadway Bridge Design Code provides design provisions to carry out such ‘No Collapse Design’ with a ductile mechanism and response modification factors given for connections and substructure play key role in this procedure. In case of response modification factors for substructure, the Roadway Bridge Design Code provides values considering ductility and redundancy. On the other hand, ‘AASHTO LRFD Bridge Design Specifications’ provides values considering additionally an artificial factor according to the bridge importance categories divided into critical, essential and others. In this study, a typical bridge with steel bearing connections and reinforced concrete piers is selected and different response modification factors for substructure are applied with design conditions given in the Roadway Bridge Design Code. Based on the comparison study of the design results, supplementary measures are suggested required by applying different response modification factors for substructure.

Anthracene has been a motive molecule for the blue-emitting materials in OLED. Since the blue emission needs big band gap between HOMO and LUMO, the blue-emitting materials are rare. In this paper, some anthracene derivatives containing simple aryl groups are synthesized and characterized. Regardless of the substituents the absorption and the emission bands are similar to each other and similar to the derivatives with the bulky silyl groups. The thermal and the CIE tests imply that among the tested 9-(2-naphthyl)-10-phenylanthracene is most promising for the diode. The material for the emission layer has to be investigated, which is simple to be prepared as well as good in the electrical and the thermal properties.

Al2O3 nanosol dispersed under ethanol or N-Methyl-2-pyrrolidone(NMP) was studied and optimized with various dispersion factors and by utilizing the silane modification method. The two kinds of Al2O3 powders used were prepared by thermal decomposition method from aluminum ammonium sulfate(AlNH4(SO4)2) while controlling the calcination temperature. Al2O3 sol was prepared under ethanol solvent by using a batch-type bead mill. The dispersion properties of the Al2O3 sol have a close relationship to the dispersion factors such as the pH, the amount of acid additive(nitric acid, acetic acid), the milling time, and the size and combination of zirconia beads. Especially, Al2O3 sol added 4 wt% acetic acid was found to maintain the dispersion stability while its solid concentration increased to 15 wt%, this stability maintenance was the result of the electrostatic and steric repulsion of acetic acid molecules adsorbed on the surface of the Al2O3 particles. In order to observe the dispersion property of Al2O3 sol under NMP solvent, Al2O3 sol dispersed under ethanol solvent was modified and solventexchanged with N-Phenyl-(3-aminopropyl)trimethoxy silane(APTMS) through a binary solvent system. Characterization of the Al2O3 powder and the nanosol was observed by XRD, SEM, ICP, FT-IR, TGA, Particles size analysis, etc.

이 연구의 목적은 폴리머의 물리적, 화학적 방법을 통해 막증류 법에 사용되는 막의 소수성 향상시킴으로써 막의 젖음 현상을 개선하는 것을 목표로 한다. 막의 소수성을 향상시키기 위해, 폴리머에 소수성을 향상 시켜줄 수 있는 시약 을 화학적 결합 또는 물리적 섞음 방법을 통해 개질을 한다. 화학적 결합으로는 styrene, pentafluorostyrene 등을 ATRP(atom transfer radical polimerization)를 통해 합성하고, 물리적 섞음으로는 PTFE(poly tetra fluoro ethylene)을 섞어 준비하였다. 두 방법 모두 평막을 제조하여 ft-ir로 결과를 확인하였고, 접촉각을 측정해 소수성을 평가하는 것으로 폴리머의 소수성 향상 여부를 확인하였다.

본 연구에서는 친수성을 가지고 있으며 외부 온도에 따라 형태를 변하는 특성을 가지는 N-isopropylacrylamide (NIPAM)를 이용하여 상용화 된 정삼투막인 HTI 분리막에 표면 개질을 하고 그에따른 표면 및 투과 특성 변화를 고찰 하고자 한다. 표면 개질을 확인 하는 방법으로 푸리에 변환 적외선 분광기 (FT-IR) 및 광전자분광기 (XPS)를 이용하였으며, 이러한 표면 개질이 정삼투 공정에 미치는 영향을 알아보기 위하여 표면의 친수성을 측정 할 수 있는 접촉각 측정 및 수투과도/Reverse salt flux와 같은 투과 특성 평가를 이용 하였다. 위와 같은 표면 및 투과 특성 평가를 바탕으로 성공적으로 표면 개질을 되었음을 증명 할 수 있었다.

기체분리막에 널리 사용되는 소재인 poly(ether-b-amide)는 고분자 사슬 내 아마이드기 간의 수소결합으로 인해 crystallinity가 높아 투과도가 낮은 것으로 알려져 있다. 본 연구는 수소결합과 그에 따른 crystallinity를 줄여 투과도를 향상시키려 한다. 이를 위해 poly(ether-b-amide)의 아마이드기를 N-alkoxymethyl로 치환하여 수소결합을 방해한다. 개질된 poly(ether-b-amide)로 재조된 기체분리막의 crystallinity는 감소하고, 투과도는 향상되길 기대한다. 현재 N-methoxymethyl group이 치환된 정도에 따른 poly(ether-b-amide)들의 기체 투과특성을 평가 중이다.

Membrane distillation (MD) is a hydrid membrane process using the temperature difference as a driving force. In order to enhance the performance (flux) of the MD process, various membrane structures (asymmetric or bi-composite) and materials (PP, PVDF or PTFE) have been suggested. In this study, the support layer of the commercial PTFE/PP bi-composite membrane is modifed by forming the macro punctures in it. The size and location of macro punctures were varied according to the designed support layer porosities (50, 60, 70 and 80 %). The modified membrane test was conducted by using the DCMD configuration. The flux of a modified membranewas enhanced up to 27 % compared with that of pristine membrane when the size of the macro puncture and overall porosity of the support layer were larger than 20 mm2 and 60 %, respectively.

Heterogeneous nuclear ribonucleoprotein A2/B1 (hnRNP A2/B1) have a important role in influence of pre-messenger RNA (pre-mRNA) processing and mRNA metabolism and transportation in cells. Recently, hnRNP A2/B1 can recognize m6A modifications on pre-mRNA or pre-miRNA and affect alternative splicing and miRNA processing in HeLa Cells. However, roles of hnRNP A2/B1 in various cells and tissues, especially in elary embryo development, are unclear. Here, we investigated the temporal and spatial expression patterns of hnRNPA2B13 during mammalian early embryo development. In mouse, hnRNPA2B1 was localized at the nucleus after 1-cell stage, however, hnRNPA2B1 was expressed after 2-cell stage in pig. Then, knockdown of hnRNP A2/B1 induced by RNA interference (RNAi) was used to analyze the effect of hnRNP A2/B1 in preimplantation develop in pigs. Knockdown of hnRNP A2/B1 delayed embryo development. Interestingly, ICM marker OCT4 and Sox2 was significantly decreased in blastocyst stage. mRNA expression show that transcription factors which is Pou5f1, Sox2, Nanog, Cdx2 and AP2γwas decreased the transcription levels without the changing of junction protein, ZO-1, occludin, and CXADR. Outgrowth results indicated that knock-down of hnRNPA2B1 embryos cannot format the colony. Knock-down of Methyltransferase like 3(METTL3) embryos mislocalized the hnRNPA2/B1 at the nucleus. In summary, the expression patterns of hnRNPA2/B1 differ between mouse and porcine embryos, and these differences may reflect species-specific functions during preimplantation embryo development. Our results suggested that hnRNPA2/B1 is necessary for newly synthesis of mRNA related with transcription factor, and early embryo development by the RNA epigenetic modification.

α-solanine is toxic to human health by disturbing digestive and central nervous systems. However, little information has been focused on investigated with respect to α-solanine influence in mammal oocyte maturation and quality. In this study, we investigated the effects of α-solanine on oocyte maturation, quality and possible molecular mechanisms in a pig model. Porcine Cumulus-oocyte complexes (COCs) were treated with increasing concentration (0, 1, 10, 20, 50 μM) of α-solanine subjected to further in vitro maturation culture. The result showed that α-solanine significantly inhibited cumulus cells expansion and increased oocyte death rates when the concentration of α-solanine more than 10 μM. After cell cycle and cytoskeleton analysis, the results showed that α-solanine (10 μM) disturbed meiotic resumption, increased abnormal spindle formation and cortical granules (CGs) distribution rates when compared with the untreated group. α-solanine (10 μM) triggered autophagy by increasing the expression of autophagy-related genes (LC3, ATG7, LAMP2) and accumulation of LC3-specific puncta (an autophagy maker). TUNEL staining assay showed that α-solanine significantly increased apoptosis in porcine oocytes confirmed by up-regulated the levels of BAX and CAPS3 genes. Further study revealed that exposure α-solanine (10 μM) to porcine oocytes induced ROS generation, reduced mitochondrial membrane potential. In addition, our results suggested that α-solanine (10 μM) significantly increased the levels of H3K36me3 and H3K27me3 in porcine oocytes. Taken together, these data indicated that α-solanine toxic impaired oocyte maturation and quality by inhibited cumulus cells expansion, increased abnormal spindle and CGs distribution rates, triggered autophagy/apoptosis occur, accumulated ROS, decreased mitochondrial membrane potential, and changed epigenetic modifications.

마이크로지르코니아는 높은 내약품성, 높은 전기저항성 등의 우수한 열적 기계적 성질을 가지 므로 다양한 분야에 사용되어 진다. 또한 지르코니아 표면을 친수화시키면, 물에 대한 분산성이 우수하 여 분산이 용이할 뿐만 아니라 대부분의 오염물질은 소수성을 띄기 때문에 오염물질에 대한 저항성을 높일 수도 있다. 본 연구에서는 지르코니아 표면에 γ-aminopropyltrimethoxysilane (APS)을 사용하여 서로 다른 pH 조건에서의 가수분해와 축합반응을 통한 친수성기의 도입과 물에 대한 분산성을 조사하 고 γ-ureidopropyltrimethoxysilane (UPS)을 사용한 결과와도 비교하였다.친수화로 개질된 마이크로지르코니아에의 지르코니아 표면의 수산기와 가수분해된 실란의 수산기와의 공유결합의 존재는 FT-IR ATR spectroscopy 및 ninhydrin 반응을 통해 확인하였다. 그러나, SEM/EDS의 결과로는 지르코니아 표면에 도입된 Si의 존재는 확인할 수 없었다. 또한, 입도 분석 결과 마이크로지르코니아는 개질 반응 중 일부 입자의 파쇄 및 aggregation이 일어남을 알 수 있었다. APS 로 개질한 경우 pH가 중성일 때 수분산성이 향상되었으나, 0.5~2% 농도의 UPS로 개질된 경우는 모든 경우 수분산성이 향상되며 분산안정성도 우수하였다.

Small-size buildings are not designed by professional structural engineers in Korea. Therefore, their seismic performance can not be exactly estimated because their member sizes and reinforcement may be over- or under-designed. A prescriptive design criteria for the small-size buildings exists, but it also provides over-designed structural members since structural analysis is not incorporated, so it is necessary to revise the prescriptive criteria. The goal of this study was to provide an information for the revision, which is seismic performance and capability of small-size reinforced concrete moment frame buildings. For the study, the state of existing small-size reinforce-concrete buildings such as member size and reinforcement was identified by investigating their structural drawings. Then, over-strength, ductility and response modification factor of the small-size reinforced concrete moment frame buildings were estimated by analytical approach along with seismic performance check. The result showed that they possess moderate over-strength and ductility, and may use slightly increased response modification factor.

현재까지 상당한 기술적인 진보가 있어왔지만, 연구개발의 커다란 기술적 어려움으로 꼽히는 것은 오염물질의 비가역적인 흡착에 의한 분리막 오염과 이로 인한 시스템 성능 저하이다. 이러한 문제점을 해결하기 위한 방안으로 redox 반 응을 이용한 표면개질을 통해 분리막의 표면을 산화/환원 반응을 통해 개질하는 것으로서, 고분자 분리막의 탄소를 바탕으로 음이온 및 양이온을 가진 작용 기를 순차적으로 중합하여 오염물질과 분리막의 전기적 반발력을 향상시켜 분리막의 표면 오염을 저감하는 것이다. 본 연구에서는 양이온, 음이온성 오염물 질을 동시에 제거할 수 있는 표면개질 방법을 개발하고자 redox 반응을 이용한 접목중합을 통해 고분자 분리막의 표면을 개질하는 연구를 수행하였다.

본 연구에서는 역삼투막의 내오염성을 향상시키기 위해 실란 커플링제로 표 면 개질하여 steric hinderance를 일으키고 에폭시 코팅으로 친수성을 향상시키고자 하였다. 상용 역삼투막을 UV로 식각하여 표면을 활성화한 후 말단기가 다 른 실란 커플링제를 sol-gel 공법으로 표면 개질하고 에폭시를 이용하여 코팅하였다. 그 결과, 친수성 및 내오염성이 향상된 것을 확인하였고, FT-IR, SEM, XPS 를 통해 막의 특성을 분석하였다.

이 연구의 목적은 폴리머의 물리적 혼합 또는 화학적 합성 방법을 통해 막증류 법에 사용되는 막의 소수성을 변화시킴으로써 막증류법의 수투과도 변화를 측정 하고자 한다. 막의 소수성을 향상시키기 위해, 물리적 혼합 방법으로 PTFE 을 섞어 준비하였고, 화학적 결합 방법으로는 Styrene, pentafluorostyrene 등을 ATRP 방법을 통해 합성하여 막을 준비하고, 그에 따른 화학적 구조를 FT-IR로 확인하였다. 두 방법을 통해 준비된 중공사 막을 MD에 적용하였을 때 순수 막과 비교하여 소수성 및 성능의 향상 여부를 확인하였다.