This paper was examined the durability properties of concrete using rapid cooling slag as fine aggregate for concrete. The results of experiments, concrete using rapid cooling slag showed that durability properties was equal to concrete using normal fine aggregate.

Method for Protect of the river levee was method for installing concrete revetment block and concrete mat method in Korea. But this method is non-environmental approach because the vegetation can not take at all. To solve these problem, the method has been applied using porous vegetation concretes. Porous vegetation concrete has filler technique to provide water retention and nutrient a into the porous interior in order to facilitate plant growth. But filler used increasing the cost and the construction period. Therefore in order to not use a filler, a high absorption rate and good absorption capacity needed aggregate. Current, Blast furnace slag aggregate has been used in architectural and civil engineering field as an alternative aggregate resources. Blast furnace slag aggregate is high absorption rate and lighter in weight per unit. This study evaluated the absorption capacity of the blast furnace slag aggregate. Phosphorus Sorption experiment was carried out to produce a cylindrical acrylic(diameter 11cm, height 90cm). There filling the aggregate, for supplying the test solution was using as a pump from bottom to top. And The water of having passed through the solution was analyzed. Results, blast furnace slag aggregate showed absorption capacity of 64~77% of PO43-P and T-P. Crushed aggregate show absorption capacity of 6~24% of PO43-P and T-P. Blast furnace slag aggregate showed excellent result of good absorption capacity compared to the crushed aggregate showed excellent result.

This paper was examined the mechanical properties of concrete using rapid cooling slag as fine aggregate for concrete. The results of experiments, concrete using rapid cooling slag showed that mechanical properties was equal to concrete using normal fine aggregate.

본 연구에서는 표준실험체 (BSS), 순환굵은골재와 고로슬래그 미분말의 치환과 하이브리드섬유를 보강한 실험체 (BSPRR1, BSPRR2시리즈), 순환굵은골재와 고로슬래그 미분말의 치환과 PVA섬유를 보강한 실험체 (BSPG시리즈)로 총 13개의 실험체를 실물크기의 1/2로 축소 제작하여 실험을 수행하였다. 실험을 통하여 얻어진 결과를 비교⋅분석하여 하중-변위, 파괴형태, 최대내력 등을 규명함으로써 구조성능의 개선정도를 평가하였다. 실험결과 순환굵은골재와 고로슬래그 미분말을 치환한 콘크리트에 하이브리드섬유를 보강한 실험체 (BSPRR1, BSPRR2시리즈)의 경우 표준실험체 (BSS)에 비하여 압축강도는 최대 13%, 최대내력은 4~21%, 연성능력은 각각 4~28% 증가하는 결과를 나타내었다. 그리고 또한, 충분한 연성적인 거동과 안정적인 휨인장 파괴를 나타내었다.

In this study, the concrete compressive strength test conducted according to the replacement ratio of electronic arc furnace oxidizing slag. As higher substitution rate of the electronic arc furnace oxidizing slag aggregates, early concrete compressive strength development is effective and the higher the concrete compressive strength as too.

최근 골재 수급불균형 문제 및 천연자원 고갈에 관한 사회적 관심이 집중되는 가운데, 종래 철강공정에서 부산물로 발생하는 슬래그 중 전기로 산화슬래그는 그 물리적 특성이 일반 골재와 유사한 특성이 있어 콘크리트용 골재로서 활용가능성이 높게 평가되나 슬래그 중 함유되어 있는 free-CaO에 의한 표면결함을 야기하는 문제를 내재하고 있다. 본 연구는 이러한 전기로 산화슬래그 골재의 화학적 안정성 확보 방안을 도출하고 이를 통해 안정화된 슬래그 골재를 용도별 콘크리트용 잔골재로 활용하여 콘크리트의 역학적 성능 및 내구성능을 실험적으로 평가함으로서 최종적으로 전기로 산화슬래그 잔골재의 활용방안을 제시하는 데 그 목적이 있다. 본 연구결과, 전기로 산화슬래그의 골재입경 조정, 소정 기간 동안의 자연 에이징 처리에 의해 팝아웃 등의 표면결함을 대폭 저감할 수 있는 것으로 나타났으며, 콘크리트 용도별 대체율에 따른 역학적 성능 및 내구성능은 일반 골재와 비교하여 동등 또는 동등 이상의 성능을 발현하는 것으로 평가되었다. 향후 전기로 산화슬래그 잔골재 활용시에는 콘크리트의 미관저해 현상이 나타나지 않도록 충분한 사전 에이징 또는, 가공처리 등 안정성 확보를 위한 품질관리가 선행되어야 할 것이다. 또한, 철강부산물의 친환경적인 자원순환 시스템을 확립하기 위해서는 전기로 산화슬래그 골재에 대한 품질관리방안 확립과 더불어 다양한 용도개발이 이루어져야 하며 각종 공학적 특성 및 내구성에 관한 지속적인 연구개발이 이루어져야 할 것이다.

본 연구는 수산화나트륨(NaOH)으로 활성화된 알칼리 활성화 슬래그 시멘트(alkali-activated slag cement; AASC)의 기초 특성에 관한 실험에 관한 연구이다. 물-결합재 비(W/B)를 0.4와 0.5로 하였다. 그리고 활성화제의 농도를 2M과 4M을 사용하였다. 각 W/B 비에 대해5가지의 배합을 고려하였다. N0는 KS L 5109의 방법이고 N1~N4는 배합시간, 배합 단계 그리고 잔골재의 투입시점을 다르게 변화시켰다. 시험결과 AASC의 플로우 값, 강도 그리고 건조수축은 잔골재의 투입시점에 영향을 받았다. 플로우 값은 잔골재의 투입시점이 늦춰짐에 따라 감소하는 경향을 나타내었다. 압축강도와 휨강도는 투입시점이 늦어짐에 따라 증가하였다. 더구나 XRD 분석은 이러한 결과들을뒷받침하고 있었다. 건조수축은 잔골재의 투입시점이 늦어지면 증가하였다. 본 연구에 고려된 실험요인들을 통해 배합을 조절한다면 AASC의 특성을 향상시킬 수 있을 것이다.

This study investigates the fundamental properties of the water-binder (W/B) ratio and fine aggregate-binder (F/B) ratio in the alkali-activated slag cement (AASC) mortar. The W/B ratios are 0.35, 0.40, 0.45, and 0.50, respectively. And then the F/B ratios varied between 1.00 and 3.00 at a constant increment of 0.25. The alkali activator was an 2M and 4M NaOH. The measured mechanical properties were compared, flow, compressive strength, absorption, ultra sonic velocity, and dry shrinkage. The flow, compressive strength, absorption, ultra sonic velocity and dry shrinkage decreased with increases W/B ratio. The compressive strength decreases with increase F/B ratio at same W/B ratio. Also, at certain value of F/B ratio significant increase in strength is observed. And S2 (river sand 2) had lower physical properties than S1 (river sand 1) due to the fineness modulus. The results of experiments indicated that the mechanical properties of AASC depended on the W/B ratio and F/B ratio. The optimum range for W/B ratios and F/B ratios of AASC is suggested that the F/B ratios by 1.75~2.50 at each W/B ratios. Moreover, the W/(B+F) ratios between 0.13 and 0.14 had a beneficial effect on the design of AASC mortar.

Replacement aggregate source like as electric arc furnace slag will be important more and more in the domestic construction field. Recently KS F 4715 was revised in order to utilize electric arc furnace slag as concrete aggregate. However, stability for an actual structure has not been confirmed sufficiently. Therefore, more careful attention should be paid on the quality management of slag aggregate. To evaluate the volume stability of electric arc furnace slag, a method of immersion expansion for evaluating road aggregate has been used. These conventional method needs long time, so there are many demands from industry for fast testing method. This paper is intended to evaluate whether the acceleration test method in the hydro thermal condition is proper or not, and find the correlations between the volume expansion and oxide compounds of slag aggregate. The test results indicates that the acceleration test method has sufficient possibility as a way of evaluating the safety of electric arc furnace slag, and that there is no correlations between the volume expansion of mortar bar with slag aggregate and the oxide compositions of slag aggregate, but the main cause of the pop-out phenomenon is the MgO content of slag aggregate.

For utilization of Electric Arc Furnace Slag’s high added value, KS F 4571 was revised, so the institutional environment to use concrete aggregate was prepared. But, it has hardly been reported how much the slag occurring in actual steel-making plants meets KS requirements. Therefore, this study was intended to analyze various engineering features of electric arc furnace slag, which occur in diverse kinds of electric arc furnace process to manufacture reinforcing rebar, hot roll, and shape steel, in accordance with KS and relevant standards. The test results from this study showed that electric arc furnace slag occurring in Korea didn’t meet the standards relating to many physical properties, such as water absorption, grading, unit volume weight, and material passing standard sieve 0.08 mm which are required for concrete aggregate and are prescribed in KS F 4571, and therefore that something is needed to be improved. Regarding chemical properties, heavy metal solubility based on official wastes test method, CaO and FeO were met, but content of MgO related to expansion and basicity exceeded or came close to standards. Therefore, it was found that some measures should be taken to address the issue.

고로슬래그 미분말을 순환골재 모르타르 및 콘크리트의 제조에 활용할 경우, 순환골재에서 용출된 Ca(OH)2가 고로슬래그에 대한 자극제 역할을 수행하여 수화반응을 개선할 수 있을 것으로 판단되고 고로슬래그를 통해 알칼리 저감 효과를 얻을 것으로 예상되어 본 연구를 진행하게 되었다. 그 결과 고로슬래그 미분말을 혼입․사용한 순환 잔골재 모르타르는 재령 3일에서는 고로슬래그 혼입율에 따라 강도가 감소하는 결과를 나타냈다. 이는 고로슬래그의 수화반응이 일어나지 않았기 때문으로 판단되며 또한, 순환 잔골재 혼입률에 관계없이 고로슬래그 미분말의 혼입률이 증가함에 따라 재령 3일 측정한 수화활성도도 저하되는 것으로 나타났다. 재령 7일에서는 순환 잔골재에서 용출된 수산화칼슘(Ca(OH)2)이 자극제 역할을 수행하여 고로슬래그 미분말을 혼입한 배합의 압축강도 발현이 천연 잔골재를 사용한 모르타르보다 서서히 증가하는 결과를 보이기 시작하였으며 이로 인해 재령 7일 측정한 고로슬래그 미분말을 단계별로 혼입한 배합의 수화활성도가 고로슬래그를 혼입하지 않은 배합보다 높아지는 것으로 나타났다. 재령 28일에서는 고로슬래그 미분말 혼입률 30% 배합에서는 고로슬래그의 수화반응으로 인해 천연 잔골재를 사용한 배합보다 높은 압축강도를 보이기 시작하였으며 이때 측정한 수화활성도는 천연 잔골재를 사용한 배합과 특별한 차이를 보이지 않았으며, 이는 지속적으로 수산화칼슘(Ca(OH)2)이 공급되지 못하였기 때문으로 판단된다.

최근 들어 정부의 환경정책이 폐기물의 발생량을 줄이되 발생되는 산업부산물을 적극적으로 재활용하는 자원순환형 폐기물 관리로 추진됨에 따라 산업 각 부분에서 발생되는 산업부산물의 재활용에 대한 연구 및 적용성이 활발히 진행되고 있다 최근 잔골재의 대체재로 주목 받고 있는 동슬래그는 본격적인 활용이 진행된다면 잔골재 수급에 많은 도움을 줄 것으로 예상되나 천연골재에 비해 높은 비중 및 대체율이 30%를 초과하면 재료분리가 발생하는 등의 단점 또한 지적되고 있다 본 연구에서는 동슬래그의 혼입 시 발생되는 블리딩의 발생을 혼화제의 사용을 통하여 억제하고 압축강도 시험 결과 등의 종합적인 고찰을 통하여 잔골재 대체시의 동슬래그의 적정 혼입률을 도출하고자 하였다