A new approach to produce nanostructured WC/Co composite powders by a mechanochemical process was made to improve the mechanical properties of advanced hardmetals. Homogeneous spherical W-Co salt powders were made by spray drying of aqueous solution from ammonium metatungstate(,AMT) and cobalt nitrate hexahydrate (Co(NO).6). spray dried W-Co salt powders were calcined for 1 hr at in atmosphere of air. The oxide powder was mixed with carbon black by ball milling and this mixture was heated with various temperatures and times in . The composite oxide powders were obtained by calcinations at . The primary particle size of W/Co composite oxide powders by SEM was 100 nm. The reduction/carburization time decreased with increasing temperatures and carbon additions. The average size of WC particle carburized at by TEM was smaller than 50 nm.