The synthesis and consolidation of titanium silicide by electro-discharge-sintering has been investigated. As-received Ti powder was in flaky shape and the mean particle size was , whereas the mean particle size of the pre-milled Si powder with angular shape was . Single pulse of 2.5 to 5.0 kJ/0.34g-elemental Ti and pre-milled Si powder mixture with the composition of Si was applied using capacitor. The solid with phase has been successfully fabricated by the discharge with the input energy more than 2.5kJ in less than Hv values were found to be higher than . The formation of occurred through a fast solid state diffusion reaction.