The likelihood of failure by the corrosion of high temperature H2S/H2, which affect to a risk of facilities, was analyzed through the risk based-inspection using API-581 BRD. We found that the corrosion rate was increased as temperature and H2S concentration were increased. Also, the technical module subfactor(TMSF) was increased as an used you increased, material thickness decreased, inspection number decreased, and inspection effectiveness increased. In these conditions, the maximum value of TMSF was not varied, but the TMSF was sensitively varied at low temperature for high concentration of H2S.