Two-component polyurethane flame-retardant coatings were prepared by blending trichloro aromatic modified polyesters(TCMPs) and polyisocyanate. TCMPs were synthesized by polycondensation of trichlorobenzoic acid(TCBA), a flame-retardant component, with adipic acid, 1,4-butanediol, and trimethylolpropane. The content of TCBA was varied in 10, 20, and 30 wt% for the reaction. These new flame-retardant coatings showed various properties comparable to other non-flame-retardant coatings. Moreover, we carried out the combustion test and the flammability test for our flame-retardant coatings. The results of vertical burning test for the coatings containing more than 20 wt% of TCBA were determined as 'no burn'. The results of flammability test for the coatings with 20 wt% and 30 wt% of TCBA contents indicated the limiting oxygen index(LOI) values of 25% and 28% respectively, which implied relatively good flame retardancy.