Acrylic pressure sensitive adhesives of n-butyl acrylate, 2-ethyl acrylate, methyl acrylate, vinyl acetate, acrylic acid, acrylonitrile and 2-hydroxyethyl acrylate were synthesized and basic physical properties of pressure sensitive adhesives with increasing the contents of 2-hydroxyethyl acrylate were investigated. 2-Hydroxyethyl acrylates effects on glass transition temperature, viscosity, hardening time and peel strength. Glass transition temperature(Tg) decreased with increasing the contents of 2-hydroxyethyl acrylate. Viscosity and hardening time were increased with increasing the contents of 2-hydroxyethyl acrylate. On the other hands, peel strength increased with increasing the contents of 2-hydroxyethyl acrylate up to 6 wt% and the decreased at further higher contents of 2-hydroxyethyl acrylate. In peel test, interfacial failure was occured in 8 wt% and 10wt%.