To prepare an acrylic type pressure-sensitive adhesive, quarternary polymers were synthesized from butyl acrylate (BA), 2-ethyl hexyl acrylate (2-EHA), methyl methacrylate (MMA), and 2-hydroxy ethyl methacrylate (2-HEMA). The quarternary polymers were identified by FT-IR and Molecular weight was measured by Gel Pearmeation Chromatography. Also, viscosity, solid content and peel strength were examined. The peel strength was 160 gf/25 mm when the volume ratio of feed monomer to solvent was 1.3:1, and the ratio was relevant to commercial usage. The pot life of adhesive was 30 sec at the 50 m/min of heat treatment rate at, and it indicated that the minimum drying time was 30 sec. In weathering resistance test, peel strength of 160~180 gf/25 mm after 1000 h, with no residual remains on the adhesive surface.