To prepare a solution type acrylic pressure-sensitive adhesive, quarter polymers were synthesized from butyl acrylate(BA), 2-ethylhexylacrylate(2-EHA) as a base monomer, methyl methacrylate(MMA) as a comonomer, each of methacrylic acid(MAA), acrylic acid(AA) as a functional monomer. Acrylic solution type pressure-sensitive adhesives(PSA's) of isocyanate derivative crosslinking PSA's were prepared by crosslinking of BEMM, BEMA with toluene-2,4-diisocyanate. The structure of adhesive was identified by FT-IR. The viscosity was measured by using Brookfield DV-III and molecular weight was measured by using gel permeation chromatography. The physical properties of polyethylene film coated with BEMMT, BEMAT were measured as a function of the concentration. As the result, BEMMT(0.6, 0.8), BEMAT(0.6) showed peel adhesion of 160~180 gf/25 mm width and shear adhesion of more than 24 hours, and tackiness of 4/32~6/32 which was relevant to commercial usage.