The influence of red lead(Pb3O4) to curing and formation reaction properties when it was added in positive material of lead acid battery for vehicle use has been investigated. At the results, it was confirmed that the addition of red lead led 4BS crystal size to be smaller and increased the rates of 4BS formation and Pb consumption. Consequently the curing time was shortened to half compared with that of red lead-free one. In addition to this, the lead acid battery prepared by adding red lead showed 14% higher efficiency at the life cycle test than that without red lead.