pp.197-202
Positive plate was composed of lead hydroxide via reaction between lead oxide and H2O and lead sulfate was formed of the reaction of lead hydroxide with sulfuric acid. And its density is 3.8 g/cm3, 4.0 g/cm3, 4.2 g/cm3 and 4.4 g/cm3 by controlling volume of refined water. Curing of positive plate is done for low (45℃, 40hr, over 95% of relative humidity) & high (80℃, 40hr, over 95% of relative humidity) temperature, which created 3BS & 4BS active materials. Experimental result of DOD with 100% life cycle test shows that it was not related to the density of active materials but to the low & high temperature aging of active materials. The test makes us to understand that the crystallization which is made by curing of active materials is a more of a main factor than density of active materials under the deep cycle using circumstances. The active materials which were from the high temperature curing are better for deep cycle performance.