pp.522-526
Graphene has been effectively synthesized on Ni/SiO2/Si substrates with CH4 (1 SCCM) diluted in Ar/H2(10%) (99 SCCM) by using an inductively-coupled plasma-enhanced chemical vapor deposition. Graphene was formed on the entire surface of the 500 nm thick Ni substrate even at 700 ˚C, although CH4 and Ar/H2 gas were supplied under plasma of 600 W for 1 second. The Raman spectrum showed typical graphene features with D, G, and 2D peaks at 1356, 1584, and 2710 cm-1, respectively. With increase of growth temperature to 900 ˚C, the ratios of the D band intensity to the G band intensity and the 2D band intensity to the G band intensity were increased and decreased, respectively. The results were strongly correlated to a rougher and coarser Ni surface due to the enhanced recrystallization process at higher temperatures. In contrast, highquality graphene was synthesized at 1000 ˚C on smooth and large Ni grains, which were formed by decreasing Ni deposition thickness to 300 nm.