논문 상세보기
pp.364-369
A SrAl2O4:Eu2+,Dy3+ phosphor powder with stuffed tridymite structure was synthesized by glycine-nitratecombustion method. The luminescence, formation process and microstructure of the phosphor powder were investigated bymeans of X-ray diffraction (XRD), scanning electron microscopy (SEM) and photoluminescence spectroscopy (PL). The XRDpatterns show that the as-synthesized SrAl2O4:Eu2+,Dy3+ phosphor was an amorphous phase. However, a crystalline SrAl2O4phase was formed by calcining at 1200oC for 4h. From the SEM analysis, also, it was found that the as-synthesizedSrAl2O4:Eu2+,Dy3+ phosphor was in irregular porous particles of about 50µm, while the calcined phosphor was aggregated inspherical particles with radius of about 0.5µm. The emission spectrum of as-synthesized SrAl2O4:Eu2+,Dy3+ phosphor did notappear, due to the amorphous phase. However, the emission spectrum of the calcined phosphor was observed at 520nm(2.384eV); it showed green emission peaking, in the range of 450~650nm. The excitation spectrum of the SrAl2O4:Eu2+,Dy3+phosphor exhibits a maximum peak intensity at 360nm (3.44eV) in the range of 250~480nm. After the removal of the pulseXe-lamp excitation (360nm), also, the decay time for the emission spectrum was very slow, which shows the excellent long-phosphorescent property of the phosphor, although the decay time decreased exponentially.