La2NiO4+δ세라믹스의 유전이완 및 전기전도특성 KCI 등재 SCOPUS

Dielectric Relaxation and Electrical Conduction Properties of La2NiO4+δ Ceramics

  • 언어KOR
  • URLhttps://db.koreascholar.com/Article/Detail/297225
구독 기관 인증 시 무료 이용이 가능합니다. 4,000원
한국재료학회지 (Korean Journal of Materials Research)
한국재료학회 (Materials Research Society Of Korea)
초록

Thermoelectric power, dc conductivity, and the dielectric relaxation properties of La2NiO4.03 are reported in the temperature range of 77 K - 300 K and in a frequency range of 20 Hz - 1 MHz. Thermoelectric power was positive below 300K. The measured thermoelectric power of La2NiO4.03 decreased linearly with temperature. The dc conductivity showed a temperature variation consistent with the variable range hopping mechanism at low temperatures and the adiabatic polaron hopping mechanism at high temperatures. The low temperature dc conductivity mechanism in La2NiO4.03 was analyzed using Mott's approach. The temperature dependence of thermoelectric power and dc conductivity suggests that the charge carriers responsible for conduction are strongly localized. The relaxation mechanism has been discussed in the frame of the electric modulus and loss spectra. The scaling behavior of the modulus and loss tangent suggests that the relaxation describes the same mechanism at various temperatures. The logarithmic angular frequency dependence of the loss peak is found to obey the Arrhenius law with activation energy of ~ 0.106eV. At low temperature, variable range hopping and large dielectric relaxation behavior for La2NiO4.03 are consistent with the polaronic nature of the charge carriers.

저자
  • 정우환 | Jung, Woo-Hwan