목적: 본 연구는 콘택트렌즈 재료로 널리 사용되는 2-hydroxyethyl methacrylate, N-vinyl-2-pyrrolidone, methyl methacrylate, ethylene glycol dimethacrylate에 titanium isopropoxide와 tungsten(VI) oxide 나노입자를 첨가하여 안의료용 렌즈 재료를 중합하였다. 방법: 안의료용 콘택트렌즈의 첨가제로 Tungsten (VI) oxide 나노입자 사용의 활용도를 조사하기 위해 tungsten(VI) oxide 나노입자를 포함한 하이드로젤 콘택트렌즈 재료의 광학적, 물리적 특성 변화를 측정하였다. 결과: 생성된 고분자에 대한 자외선 영역의 투과율은 매우 낮게 측정되어 자외선 차단 능력이 있는 것으로 나타났다. 또한 tungsten(VI) oxide 나노입자의 첨가는 함수율의 큰 변화를 나타내지 않았으나 일정비율을 첨가한 조합에서는 소량의 함수율 변화가 나타났다. 함수율의 큰 변화가 없음에도 불구하고 산소침투율의 측정 값은 tungsten(VI) oxide 나노입자의 첨가 비율이 증가할수록 계속적으로 감소하는 경향이 나타 났다. 결론: 이상의 결과를 통해 titanium isopropoxide 및 tungsten(VI) oxide 나노입자는 하이드로젤 콘택트렌즈의 기본적인 물성을 만족시키면서 기능성 콘택트렌즈 재료로 유용하게 활용될 수 있을 것으로 판단된다.

Purpose: The materials for ophthalmic hydrogel lenses were polymerized by adding tungsten (VI) oxide nano particles to 2-hydroxyethyl methacrylate, N-vinyl-2-pyrrolidone, methyl methacrylate and ethylene glycol dimethacrylate which are commonly used in ophthalmic contact lenses. Methods: The changes in optophysical properties of the ophthalmic contact lens containing tungsten (VI) oxide nano particles were also measured to investigate the use of tungsten (VI) oxide as an additive of hydrogel contact lenses. Results: the transmittance of UV was measured to be extremely low which shows that the nano particles can provide a UV-blocking property. Meanwhile, although the water content did not show a significant variation from the addition of tungsten (VI) oxide nano particles, water content slightly changed in combinations where tungsten nano particles were added at a constant ratio. The oxygen permeability showed to continuously decrease as the addition ratio of tungsten (VI) oxide nano particles increased even though there was no significant difference in water content. Conclusions: Titanium(IV) isopropoxide and tungsten (VI) oxide nano particles are considered to satisfy the basic requirements of ophthalmic hydrogel contact lenses and can be used effectively as additives for functional ophthalmic hydrogel lenses.

• Tae-Hun Kim(백석대학교 안경광학과) | 김태훈
• A-Young Sung(세한대학교 안경광학과) | 성아영