The aim of present work is to link geometrical parameter of maximum area of structural defect (proposed by Y. Murakami, 1983) with surface fatigue mechanisms. Determined relations allow making predictions of surface fatigue properties of cemented carbides (WC-Co hardmetal - H15 - 85wt% WC and 15wt %Co, TiC-based cermets - T60/8 - 60wt %TiC and Fe/8wt% Ni and T70/14 - 70wt %TiC and Fe/14wt% Ni) in conditions of rolling contact and impact cycling loading. Pores considered being equivalent to small defects. Three comparative defects conditions are distinguished: surface pore, just below free surface and interior pores. The Vickers hardness of binder (as main responsible for the fracture mechanism of hardmetal and cermets) assumed to be the basis of such assumption. The estimate of this prediction has been done by analyzing the pore sizes using the statistics of extremes. The lower bound of fatigue properties can be correctly predicted by considering the maximum occurring pore size.