The corrosion behavior of the Inconel X-750 alloy was investigated for its potential application under a Cl2-O2 mixed gas flow in an Ar atmosphere. The corrosion rate was found to be negligible at temperatures up to 400℃ under a flow rate of 30 mL·min-1 Cl2 + 170 mL·min-1 Ar, whereas an exponential increase was observed in the corrosion rate at temperatures greater than 500℃. The suppression of the corrosion reaction due to the presence of O2 was verified experimentally at flow rates of 30 mL·min-1 Cl2 (4.96 g·m-2·h-1), 20 mL·min-1 Cl2 + 10 mL·min-1 O2 (2.02 g·m-2·h-1), and 10 mL·min-1 Cl2 + 20 mL·min-1 O2 (1.34 g·m-2·h-1) under a constant Ar flow rate of 170 mL·min-1 at 600℃ for 8 h. The surface morphology analysis results revealed that porous surfaces with tunnel-type holes were produced under the Cl2-O2 mixed-gas condition. Furthermore, the effects of the Cl2 flow rate on the corrosion rate were investigated, indicating that its impact was negligible within the range of 5–30 mL·min-1 Cl2 at 600℃.

1. Introduction
2. Experimental
3. Results and discussion
4. Conclusions
REFERENCES

• Min Ku Jeon(Korea Atomic Energy Research Institute/University of Science and Technology) Corresponding Author
• Sung-Wook Kim(Korea Atomic Energy Research Institute)
• Sang-Kwon Lee(Korea Atomic Energy Research Institute)
• Eun-Young Choi(Korea Atomic Energy Research Institute/University of Science and Technology)