The mixed atomized iron powders with 0.3% graphite and 1% Ni powders were cold pressed and sintered at for 30 min under pure Ar gas atmosphere. Some of the sintered specimens were intercritically annealed at and quenched in water (single quenching). The other sintered specimens were first fully austenized at and water quenched. These specimens were then intercritically annealed at and re-quenched in water. The experimental results showed that the wear coefficient effectively decreased in the double quenched specimen.