The study examines hardness pattern of SH737-2Cu-.9C samples transient liquid phase sintered at different temperatures viz. , and , heat treated by various methods and then tempered at different temperatures. Sintered samples were characterized for density and densification parameter, and austenitized at , subsequently cooled by four different methods viz. annealing, normalizing, oil and brine quenching. Hardness pattern was found minimum for air cooled and maximum for brine quenched, and samples sintered at had relatively higher hardness. The O.Q and B.Q samples were then tempered at , , and . Hardness pattern typically showed secondary hardness taking place, with maximum around .