pp.45-56
PURPOSES : Given that large-scale repair works of expressway bridge pavements have high maintenance cost and long traffic blocking time, the thin overlay method that maintains the existing pavement is attracting attention. In this study, because the bridge thin overlay has not been introduced in Korea yet, the basic physical properties of the epoxy thin overlay, which is mainly used for the bridge thin overlay, were investigated, and the skid resistance and bond performance were analyzed.
METHODS : Basic physical property tests were performed on each of the epoxy binders, aggregates, and mixtures used in epoxy thin overlay. They were also compared and reviewed against foreign standards. The epoxy binders were tested for viscosity, gel time, and thermal compatibility. The aggregates were tested in terms of water absorption, specific gravity, and gradation. The compressive and flexural strengths of the mixtures were investigated. The epoxy thin overlay has the possibility of detachment of aggregates, so the skid resistance was tested according to the paving phase. In addition, to investigate the bond performance, which is the most important performance of the epoxy thin overlay, the bond strength test was performed by varying the moisture condition and treatment condition of the existing layer surface.
RESULTS : The basic physical properties of the materials used in the epoxy thin overlays satisfied foreign standards except for the gradation of aggregates. The skid resistance did not satisfy the standard when the epoxy was exposed, whereas the skid resistance did satisfy the standard when the aggregates were exposed, even after the abrasion test. The bond strength of the epoxy thin overlay satisfied the standard in all cases. The bond strength was the highest when the relative humidity of the existing layer surface was 60%.
CONCLUSIONS : The materials of epoxy thin overlay that could be obtained in Korea satisfied the basic physical property standards except for aggregate gradation. Given that the aggregate gradation could be adjusted, it can be concluded that the epoxy thin overlay could be introduced in Korea. In addition, it was confirmed that the skid resistance and bond strength of the epoxy thin overlay were high enough to be used in general road conditions. It was determined that the existing layer surface should maintain an optimal relative humidity of approximately 60% because the moisture condition affects the bond strength.
1. 서론
2. 에폭시 바인더와 골재의 물성시험
2.1. 에폭시 바인더의 선정
2.2. 에폭시 바인더, 골재, 혼합물의 재료특성 시험
3. 에폭시 도포 골재 포설물의 미끄럼저항과부착강도
3.1. 공시체 제작
3.2. 미끄럼저항 시험
3.3. 부착강도 시험
4. 결론
REFERENCES