Powder grades pre-alloyed with 1.5-3 wt% chromium can be successfully sintered at the conventional temperature although well-monitored sintering atmospheres are required to avoid oxidation. Mechanical properties of the Cr-alloyed PM grades are enhanced by a higher sintering temperature in the range , due to positive effects from pore rounding, increased density and more effective oxide reduction. Astaloy CrM (Fe-3 wt% Cr-0.5 wt% Mo) with 0.6 wt% graphite added obtains an ultimate tensile strength of 1470 MPa and an impact strength of 31 J at density , after sintering at followed by cooling at and tempering.