In order to accelerate the sintering of Al-Bronze powder covered with passive oxide film, we focused on the way to add Al-Ca fluoride consisting of and , examined the effect of the mixing rate in Al-Ca fluoride, the amount of the added Al-Ca fluoride and the sintering temperature on sintering properties of Al-Bronze powder and considered the mechanism of the sintering acceleration. Al-Bronze powder was sintered most effectively by adding Al-Ca fluoride with the mixing rate of 20mass%. If the amount of added fluoride was over 0.05mass% and the sintering temperature was over 1123K, the sintering acceleration of the Al-Bronze powder appears. Regarding the mechanism of the sintering acceleration, it was presumed that film on the surface of the Al-Bronze particles was removed in the process of the formation of gaseous AlOF by the reaction with , and the reaction was accelerated further by the presence of the liquid phase which is formed in Al-Ca fluoride.