Formation of Rod-like via Mechanical Activation Followed by Thermal Processing

  • 언어KOR
  • URLhttps://db.koreascholar.com/Article/Detail/4238
모든 회원에게 무료로 제공됩니다.
한국분말재료학회(구 한국분말야금학회) (Korean Powder Metallurgy Institute)
초록

A QM-ISP-4 Planetary Mill was employed to activate mechanically the mixtures of anatase and corundum at room temperature for different times. The milled powder mixtures were then sintered at for 1 h. The XRD results showed that the milled powder mixtures were completely transformed into after sintering, except the mixtures milled for 5 and 10 hours. The SEM observations showed the typical morphology of rod-like vary in the range: widths from 0.6 to , and lengths from 3.0 to . The rod-like formation was attributed to the positive effects caused by the mechanical activation.