In this study, we investigate the flexural bonding behavior of glass fiber reinforced polymer (GFRP) reinforced bars in a beam application. The GFRP reinforced bars were designed without end hooks. We fabricated beam specimens and subjected them to four-point bending tests. The parameter under consideration was the nominal diameter of the GFRP, with three different diameters: D13, D16, and D19. The results demonstrated a significant increase in the flexural strength of the beam when comparing D13 specimens to D16 and D19 specimens, with improvements of approximately 24.17% and 45.92%, respectively. This indicates that the strength of the specimens increases as the nominal diameter of the GFRP reinforcement increases. Notably, there was a proportional similarity in performance with respect to the nominal diameter in contrast to tensile strength.

본 연구에서는 GFRP(Glass Fiber Reinforced Polymer)를 주 보강근으로 사용하였으며, 정착길이가 없는 시험체를 제작 하여 4점 재하 휨시험을 수행하였다. 각 변수는 공칭지름이며 공칭지름 D13, D16, D19, 총 3가지의 변수로 이루어져있다. 휨 모 멘트는 공칭지름이 커질수록 약24.17%, 45.92% 강도가 증가하였으나 공칭 휨 강도를 고려하였을 때, 인장 강도와는 달리 공칭 지름에 비례하여 유사한 성능을 나타냄을 알 수 있었다. LVDT로 보강근과 콘크리트와의 부착성능을 확인하였고, 그 값은 매우 미미하며 거의 발생 되지 않은 것으로 판단된다. 또한 DIC로 시험체의 처짐을 확인하였으며, 실세 처짐 값과 유사함을 알 수 있었다.

1. 서 론
2. 실험 설계
    2.1 시험체 설계
    2.2 시험체 제작 및 실험 방법
3. 실험 결과
    3.1 재료 실험 결과
    3.2 시험체 실험 결과
4. 결 론
감사의 글

• 구종현(경상국립대학교 토목공학과 석사과정) | Gu Jong-Hyeon (Master Student, Department of Civil Engineering, Gyeongsang National University, Jinju, Korea)
• 배재호(경상국립대학교 토목공학과 석사과정) | Bae Jae-Ho (Master Student, Department of Civil Engineering, Gyeongsang National University, Jinju, Korea)
• 김상우(경상국립대학교 토목공학과 박사수료) | Kim Sang-Woo (Ph.D. Candidate, Department of Civil Engineering, Gyeongsang National University, Jinju, Korea)
• 김진섭(경상국립대학교 토목공학과 부교수) | Kim Jin-Sup (Associate Professor, Department of Civil Engineering, Gyeongsang National University, Jinju, Korea) Corresponding author