The purpose of this study was to examine whether galvanic corrosion of copper occurs by inserting a third barrier layer with a higher corrosion potential than copper between copper and cast iron when the copper layer is locally perforated by pitting or partial corrosion. A triple layer composed of copper, inserted metal, and carbon steel was manufactured by cold spray coating of inserting metal powders such as Ag, Ni, and Ti on carbon steel plate followed by Cu coating on it. First, the corrosion properties were evaluated electrochemically for each metal coating. As a result of Tafel plot anaylsis in KURT groundwater condition, the corrosion potential of Fe (-567 mV) was much lower than that of Cu (-91 mV), and the corrosion potential of Ni (-150 mV) was also lower than that of Cu. Therefore, Ni was likely to corrode before Cu. However, the corrosion current of Ni was lower than that of the Cu. In the galvanic specimen where the copper and inserting metal were exposed together, Cu-Fe was much lower corrosion potential of -446 mV, and the corrosion potential of Cu-Ti, Cu-Ni, and Cu-Ag were slightly higher than that of Cu. Therefore, it seemed that Ag, Ni, and Ti all might promote galvanic corrosion of surrounding copper when the copper layer was perforated to the inserted metal layer. If the metal insertion presented in this study operates properly, the disposal container does not need to worry about the partial corrosion or non-uniform corrosion of external copper layer.

• Jin-Seop Kim(Korea Atomic Energy Research Institute (KAERI))
• Junhyuk Jang(Korea Atomic Energy Research Institute (KAERI))
• Minsoo Lee(Korea Atomic Energy Research Institute (KAERI)) Corresponding author