Hydraulic Properties of the WRK Compacted Bentonite Core as an Engineering Barrier Material in the SNF Repository
- 언어ENG
- URLhttps://db.koreascholar.com/Article/Detail/431159
p.204
The WRK (Waste Repository Korea bentonite) compacted bentonite medium has been considered as the appropriate buffer material in the Korean SNF (Spent nuclear fuel) repository site. In this study, hydraulic properties of the WRK compacted bentonite core (4.5 cm in diameter and 1.0 cm in length) as the buffer material were investigated in laboratory experiments. The porosity and the entry pressure of the water saturated core at different confining pressure conditions were measured. The average velocity of water flow in the WRK compacted bentonite core was calculated from results of the breakthrough curves of the CsI aqueous solution and the hydraulic conductivity of the core was also calculated from the continuous flow core experiments. Because various gases could be generated by continuous SNF fission, container corrosion and biochemical reactions in the repository site, the gas migration property in the WRK compacted bentonite core was also investigated in experiments. The gas permeability and the average of gas (H2) in the core at different water saturation conditions were measured. Laboratory experiments with the WRK Compacted bentonite core were performed under conditions simulating the DGR environment (confining pressure: 1.5- 20.0 MPa, injection pressure: 1.0-5.0 MPa, water saturation: 0-100%). The WRK Compacted bentonite core was saturated at various confining pressure conditions and the porosity ranged from 27.5% to 43.75% (average: 36.75%). The calculated hydraulic conductivity (K) of the core using experimental results was 8.69×10-11 cm/s. The gas permeability of the core when the water saturation 0~58 % was ranged of 19.81~3.43×10-16 m2, representing that the gas migration in the buffer depends directly on the water saturation degree of the buffer medium. The average gas velocity in the core at 58% of water saturation was 9.8×10-6 m/s, suggesting that the gas could migrate fast through the buffer medium in the SNF repository site. Identification of the hydraulic property for the buffer medium, acquired through these experimental measurements is very rare and is considered to have high academic values. Experimental results from this study were used as input parameter values for the numerical modeling to simulate the long-term gas migration in the buffer zone and to evaluate the feasibility of the buffer material, controlling the radionuclide-gas migration in the SNF repository site.