The bentonite buffer material is a crucial component for disposing of high-level radioactive waste (HLW). Several additives have been proposed to enhance the performance of bentonite buffer materials. In this study, unconfined compression tests were conducted on bentonite mixtures as well as pure bentonite buffer material. Joomunjin and silica sands were added at a 30% ratio, and graphite was added at 3% along with bentonite. The unconfined compression strength (UCS) and elastic modulus of pure bentonite were found to be 20% to 50% higher than those of bentonite mixtures under similar dry density and water content conditions. This decrease in strength can be attributed to the reduced cross-sectional area available for bearing the applied load in the bentonitemixture. Furthermore, the 3% graphite-bentonite mixture exhibited a 10% to 30% higher UCS and elastic modulus compared to the 30% sand-bentonite mixtures. However, since the strength properties of additive-bentonite mixtures are lower than those of pure bentonite, it is essential to evaluate thermohydraulic-mechanical functional criteria when considering the use of bentonite mixtures as buffer materials.

• Seok Yoon(Korea Atomic Energy Research Institute (KAERI))
• Gi-Jun Lee(Korea Atomic Energy Research Institute (KAERI)) Corresponding author
• Deuk Hwan Lee(Korea Atomic Energy Research Institute (KAERI))
• Min-Hyeong Lee(Korea Atomic Energy Research Institute (KAERI))
• Sojeong Lee(Ajou University)