Crystallographic properties of Ni-based alloys such as alloys 600, 617, and Hastelloy N, which are a candidate to be used as structural materials in Molten Salt Reactor (MSR), were studied in the temperature range of 25-1,000°C using high-temperature X-ray diffraction (HT-XRD) under an Ar atmosphere. We found that face-centered cubic Ni crystal structure at room temperature was started to be changed over 600°C in all Ni-based samples. However, the appearance of changing diffraction patterns over 600°C was different for all samples. In addition, we observed the increase in the lattice constant along the a-axis upon heating in all specimens, determined by Pawley refinement of HTXRD data.