High-frequency soft magnetic Ni, Fe, and Co-based thin films have been developed, typically as nanocrystals and amorphous alloys. These Ni, Fe, and Co-based thin films exhibit remarkably good frequency dependence up to high frequencies of several tens of MHz. These properties arise from the moderate magnetic anisotropy and fairly high electrical resistivity that result from the microstructural characteristics of the nanocrystalline and amorphous states. In this paper, Al-Co/AlN-Co and Al-N/AlN-Co multilayer films were deposited using two-facing-target type sputtering (TFTS). Their microstructures, magnetic and electrical properties were studied with the expectation that inserting Al-Co or Al-N as an interlayer could effectively reduce the coercive force and produce films with relatively high resistivity. A new approach is presented for the fabrication of Al-Co (Al-N)/AlN-Co multilayer films, prepared with the TFTS system. The deposited films were isothermally annealed at different temperatures and investigated for microstructure, magnetic properties and resistivity. The TFTS method used in this experiment is suitable for fabricating Al-Co(Al-N)/AlN-Co multilayer films with different layer thickness ratio (LTR). The annealing conditions, thickness of the multilayer film, and LTR can control the physical properties as well as the microstructure of the manufactured film. Magnetization and resistance increased and coercivity decreased as LTR decreased. The thin film with LTR = 0.175 exhibited high resistivity values of 2,500 μΩ-cm, magnetization of 360 emu/cm3, and coercivity of 5 Oe. Results suggests that thin films with such good resistivity and magnetization would be useful as high-density recording materials.
1. 서 론
2. 실험 방법
2.1. Al-Co/AlN-Co 다층 박막
2.2. Al-N/AlN-Co 다층 박막
3. 실험 결과
3.1. 증착된 Al-Co/AlN-Co 다층 박막의 일반적인 특성
3.2. 열처리 효과
3.3. Al-N/AlN-Co 다층 박막의 일반적인 특성
3.4. Al-Co/AlN-Co 다층 박막의 전도 메커니즘
4. 고 찰
4.1. Al-Co/AlN-Co 다층 박막의 결정화 거동
4.2. 나노결정 다층 박막의 연자성 특성
5. 결 론
References
<저자소개>