Effects of sintering conditions such as sintering temperature and heating rate on oxygen content, density, microstructure and toughness of sintered Mo were investigated. The oxygen content of the sintered Mo significantly depended on the sintering conditions. The oxygen content of the primary sintered(below 1673 K) Mo influenced the densifications. The number of pores at grain boundaries of the secondary sintered(at 2073 K)Mo depended on the oxygen content of the primary sintered Mo. Grain growth of the secondary sintered Mo was inhibited by the existence of pores at the grain boundaries. The secondary sintered Mo having larger number of pore and smaller grain size demonstrated higher strength.