Co-Fe-Ni-B-Si-Cr based amorphous strips containing nitrogen were manufactured via melt spinning, and then devitrified by crystallization treatment at the various annealing temperatures of for up to 30 minutes in an inert gas atmosphere. The microstructures were examined by using XRD and TEM and the magnetic properties were measured by using VSM and B-H meter. Among the alloys, the amorphous ribbons of containing 121 ppm of nitrogen showed relatively high saturation magnetization. The alloy ribbons crystallized at showed that the grain size of alloy containing 121 ppm of nitrogen was about f nm, which exhibited paramagnetic behavior. The formation of nano-grain structure was attributed to the finely dispersed Fe4N particles and the solid-solutionized nitrogen atoms in the matrix. Accordingly, it can be concluded that the nano-grain structure of 5nm in size could reduce the core loss within the normally applied magnetic field of 300A/m at 10kHz.

Polyeyclic aromatic hydrocarbons (PAHs) were quantitatively determined in bivalves from Gwangyang Bay. Twenty-four kinds of target PAHs were detected in the entire samples. Total PAHs concentrations ranged 86.1∼1,210 ng g-1/ dry weight with a average

Using a developed high-frequency induction heated combustion method. the simultaneous synthesis and densification of WC-xvol.%Co() hard materials was accomplished using elemental powders of W, C and Co. A complete synthesis and densification of the materials was achieved in one step within a duration of 1min. The final relative densities of the composite were over 98.5% for all cases, under the applied pressure of 60 MPa and the induced current. The hardness of the composites decreases and the fracture toughness increases with increasing cobalt content. As the carbon to tungsten ration increases, the hardness increase, but the fracture toughness decreases. The maximum values for the fracture toughness and hardness are 15.1 (at 20vol.%Co, W:C=1:1), and 1928 (at 5vol.%Co, W:C=1:1.3), respectively. Therefore we concluded that the HFIHCS method. which can produce WC-xvol.%Co within 1 minute in one step is superior to conventional ones.

1) Using a developed high-frequency induction heated sintering method, the rapid densification of WC-Co hard materials was accomplished using ultra fine powders with 260 nm size within 1 minute. 2) The relative density of the composite was 99.5% for the applide pressure of 60MPa and the induced current for 90% output of total capacity. 3) The grain size of WC-Co hard materials is about 260nm and the average thickness of the binder phase determined is about 11nm. The fracture toughness and the hardness of this work 12 , respectively. 4) Using pressureless sintering, we produced dense WC-Co hard materials with a relative density of 97% without applying pressure.