Compared to steel of the same weight in steel concrete structures, fiber reinforced polymer (FRP) is known to have greater strength and better resistance to corrosion. As such, it is being proposed as an effective structural material. Despite its many advantages, FRP has not been rapidly adopted in civil structures. This is because it is more expensive, prone to brittle fracture, and has weak fire resistance. To examine changes in the mechanical properties of FRP and the effectiveness of fire resistant coating, this study conducted tensile tests on coated and uncoated specimens over varying temperature. Glass fiber has excellent fire resistance since it does not melt or burn at high temperatures. However, epoxy is unable to withstand exposure to temperatures exceeding the transition temperature, thus leading to unsatisfactory structural performance and fire resistance. This study investigated the behavioral changes in FRP by exposing the specimens to temperatures ranging from room temperature (approx. 25℃) to 300℃, so as to improve the fire resistance of epoxy.

This study is a part of high strength lightweight aggregate concrete researches using lightweight aggregates and the purpose of this study is to find out the basic physical characteristics and tension cracking fracture characteristics of lightweight concrete. Crack Mouth Opening Displacement is measured through three point flexure experiment about embellish notch beam. Load-CMOD characteristics are examined through rules of countries, characteristics of lightweight concrete and tension cracking fracture experiments. The degree of tensile characteristic alteration according to size changes of specimen and the characteristics about crack surface are analyzed. The changes of softening curve are analyzed and fracture energy is drawn through inverse analysis by the obtained Load-CMOD curve. To decide fracture energy and analysis parametric, inverse analysis is conducted and Ant Colony Method is conducted for optimization and then a way to find out optimal parameterization fracture energy is suggested.

This study is to evaluate compressive behavior of confined concrete cylinders using various materials. Materials are tape, velcro, fishline, frp and scratch film. At compressive strength test result, load of confined concrete cylinder using velcro and fishline was slowly decreased after ultimate strength. Also, confined concrete cylinder using tape and frp seem to increase the compressive strength.