The purpose of this study was to investigate effect of methanolic extracts of 10 kinds of wild vegetables cultivated in Gangwon province on antioxidant activity, acetylcholinesterase, and β-secretase inhibitory activities. Results showed that among the wild vegetables, Aralia elata(Miq.) Seem shoot extract exhibited the highest total phenol content (84.65±1.08 mg GAE/g) and total flavonoids content (70.77±0.55 mg RE/g), respectively. The antioxidant activity of wild vegetables extracts was measured by using 2,2-diphenyl-1-picrylhydrazyl (DPPH) and 2,2'-azino-bis-(3-ethylbenzothiazoline-6-sulfonic acid) (ABTS) assay. Aralia elata(Miq.) Seem shoot extracts had the highest DPPH and ABTS scavenging activity (90.16%, 40.18% at 2 mg/mL). As a result, Aralia elata(Miq.) Seem shoot extract was the most effective in terms of acetylcholinesterase inhibitory activity (35.94% at 1 mg/mL). In the β-secretase activity assay, all 10 kinds wild vegetables extracts showed low inhibitory activity, and Aralia elata(Miq.) Seem shoot extract had highest inhibitory activity among the 10 wild vegetables extracts was 14.99%. Taken together, these results showed that Aralia elata(Miq.) Seem shoot extract has potential cognition improvement impact, suggesting that it may provide an effective strategy for improving cognition.

The effect of alpha phase on the fatigue properties of Fe-29%Ni-17%Co low thermal expansion alloy was investigated. Two kinds of alloys (Base alloy and Alpha alloy) were prepared by controlling the minimal alloy composition. Microstructure observation, tensile, high-cycle fatigue, and low-cycle fatigue results were measured in this study. The Base alloy microstructure showed typical austenite γ phase. Alpha alloy represented the dispersed phase in the austenite γ matrix. As a result of tensile testing, Alpha alloy was found to have higher strengths (Y.S. & T.S.) and lower elongation compared to those of the Base alloy. High cycle fatigue results showed that Alpha alloy had a higher fatigue limit (360MPa) than that (330MPa) of the Base alloy. The Alpha alloy exhibited the superior high cycle fatigue property in all of the fatigue stress conditions. SEM fractography results showed that the alpha phase could act to effectively retard both fatigue crack initiation and crack propagation. In the case of low-cycle fatigue, the Base alloy had longer fatigue life in the high plastic strain amplitude region and the Alpha alloy showed better fatigue property only in the low plastic strain amplitude region. The fatigue deformation behavior of the Fe-29%Ni-17%Co alloy was also discussed as related with its microstructure.