In this study, the purpose of this study was to develop concrete structural walls including the functions of the barrier and EMP shielding performance as the concrete structure itself. Mix of highly challenging metal fibers in super-high strength concrete. The EMP measurement frequency was evaluated for EMP card performance using a waveguide measurement method in the range of 0.8 GHz to 1.0 GHz. Performance evaluation shows that steel fiber has an increased compression strength and shielding effect as amount of mixing increases. In addition, shielding performance increased due to the increased thickness of the specimen. Therefore, it is judged that steel fiber is a good blend for shielding effects.

본 연구는 조강시멘트와 경화촉진제를 사용하여 조기강도 발현의 메커니즘을 분석하는 것이 목적이다. 연구결과 경화촉진제는 시멘트와의 수화반응시 Ca(OH)2의 촉진시키는 것을 TG/DTA 실험을 통하여 검정하였다. 압축강도 측정결과 경화촉진제의 사용량이 증가 할수록초기압축강도가 증가하는 것을 알 수 있었다. 또한 미소수화열 측정결과 경화촉진제는 시멘트의 성분중 C3S의 수화반응을 촉진시키는 것으로 나타났다. XRD분석결과 재령별 수화생성물을 확인할 수 있었으며 경화촉진제의 사용량이 증가할수록 수화물들의 피크점이 높게 나타나는 것을 알 수 있었다. SEM찰영을 한 결과 촉진제의 첨가량에 따라 Ca(OH)2의 생성과 재령에 따라 C-S-H의 형상을 관찰할 수 있었다.따라서 본 연구에서 사용된 경화촉진제는 초기강도발현 시키는 것에 대해 효과적인 것을 확인 할 수 있었다.

In this study, we investigated the physical properties and thermal behaviors of specimens that applied different mixing ratios of foaming agent to evaluate the possibility of use in the structural elements. We proposed the estimating equation for compressive strength of each mix having different ratio of foaming agent. We also confirmed that the density of cement matrix is decreased as the mixing amount of foaming agent increase up to 0.6% of foaming agent mixing ratio which was observed by SEM. Based on porosity and compressive strength of control mortar without foaming agent, we built the estimating equations of compressive strength for mortars with foaming agent

In this experiment, the high early strength cement containing massive C3S quantity was used to enhance the early strength of cement mortar using admixtures which can accelerate C3S hydration reaction in the condition of room temperature. The measuring items are zero flow, setting times, compressive strength and analysis of MIP & SEM