As ZIF materials have their unique properties such as high surface area, tunable pore structure, thermal and chemical stability, they can be used in various applications including gas separation and catalysis. For synthesis of ZIF membranes, fixing sub-micron ZIF seed particles on the support is challenging and important. In this work, ZIF-8 seed layer was synthesized by conversion synthesis of ZnO layer on support in H-mIm solution, followed by the secondary growth synthesis of ZIF-8 membranes. The parameters of conversion seeding had been investigated to control the reaction rate combining the dissolution rate of ZnO and the crystallization rate of ZIF-8. This ZIF-8 membranes showed the better coverage of seeding layer and gas separation properties compared with the membranes prepared by traditional dip-coating seeding.

MOF(Metal-organic frameworks)의 일종인 ZIF-8은 큰비표면적과 높은 열적⋅ 화학적 안정성을 가지고 있어 분리막 재료로 많은 연구가 진행되고 있다. 특히, 3.4Å 크기의 기공입구와 11.6 Å 크기의 기공 크기를 가지고 있는 ZIF-8을 분리 막으로 합성시 프로필렌/프로판을 분자체 효과를 통해 분리해 낼 수 있다. 본 연구에서는 ZnO 층을 형성하고 이를 전환시켜 결함 없는 ZIF-8 막을 합성하고 이를 통해 프로필렌/프로판을 분리하고자 했다. 우선, 매크로기공을 가진 디스크 모양의 α-알루미나 지지체 위에 ZnO 층을 형성하고, 2-methylimidazole 용액에서 용매열 합성하여 ZnO를 ZIF-8 분리막으로 전환시켰다. 합성된 ZIF-8 분리막 은 XRD, SEM, 기체투과장치, GC 등을 이용하여 분석하였다.

Zeolitic Imidazolate Framework(ZIF)는 기체의 선택적인 분리나 센서, 촉매 반응 등의 목적으로 널리 연구된다. 특히 촉매의 역할이 가능하기 때문에 반응과 동시에 가스를 분리 할 수 있는 막 반응기의 역할을 할 수 있다. 본 연구에서는 ZIF-8 입자를 합성하고, 이를 PVC-g-POEM 고분자 매트릭스에 분산하여 MMM(Mixed matrix membrane)으로 제조하였다. 특히, α-알루미나 지지체 위에 PVC-g-POEM/ZIF-8 혼합 용액을 스핀 코팅하여 균일한 두께의 MMM을 얻을 수 있었다. 합성된 MMM은 XRD, FE-SEM을 통해 결정상과 표면, 코팅 두께 등을 측정하였으며, 이성분계 기체 투과 실험을 통해 다양한 이성분계 기체에 대한 투과 특성을 살펴보았다.