Hydrogen production via high high-temperature steam electrolysis consumes less electrical energy than compared to conventional low low-temperature water electrolysis, mainly due to the improved thermodynamics and kinetics at elevated temperaturetemperatures. The elementalElemental powders of Cu, Ni, and YSZ are were used to synthesize high high-temperature electrolysis cathodecathodes, of Ni/YSZ and Cu/YSZ composites, by mechanical alloying. The metallic particles of the composites were uniformly covered with finer YSZ particles. Sub-micron sized pores are were homogeneously dispersed in the Ni/YSZ and Cu/YSZ composites. In this study, The cathode materials were synthesized and their Characterizations properties were evaluated in this study: It was found that the better electric conductivity of the Cu/YSZ composite was measured improved compared tothan that of the Ni/YSZ composite. Slight A slight increase in the resistance can be produced for in a Cu/YSZ cathode by oxidation, but it this is compensated offset for by a favorable thermal expansion coefficient. Therefore, Cu/YSZ cermet can be adequately used as a suitable cathode material of in high high-temperature electrolysis.

고상 반응법을 이용하여 L a0.6S r0.4 Co0.2F e0.8 O3-delta/ 및 L a0.7S r0.3G a0.6F e0.4 O3-delta/ 분말을 합성하고 혼합전도체 분리막을 소결하여 제조하였다. 제조된 분리막들은 정확한 페롭스카이트 결정구조를 나타내었으며, 95% 이상의 높은 상대밀도를 나타내었다. 산소이온 변환 능력을 향상시키기 위해 L a0.7S r0.3G a0.6F e0.4 O3-delta/ disk의 양 표면에 L a0.6S r0.4Co O3-delta/ paste를 스크린 프린팅 방법으로 코팅하였으며 코팅 막은 비교적 치밀한 미세구조를 나타내었다. 코팅되지 않은 L a0.6S r0.4 Co0.2F e0.8 O3-delta/ 및 L a0.7S r0.3G a0.6F e0.4 O3-delta/ 분리막과 코팅된 L a0.7S r0.3G a0.6F e0.4 O3-delta/ 분리막의 산소투과 성능을 비교 실험한 결과, 900℃에서 L a0.6S r0.4 Co0.2F e0.8 O3-delta/ 분리막이 정상상태에서 0.266 mL/min.textrmcm2로 가장 많은 투과량을 보였으며 코팅된 L a0.7S r0.3G a0.6F e0.4 O3-delta/ 분리막의 정상상태 산소 투과 유속은 최고 0.19 mL/min.textrmcm2 정도로 코팅되지 않은 분리막에 비해 약 2~3배로 높게 나타났다.정도로 코팅되지 않은 분리막에 비해 약 2~3배로 높게 나타났다.코팅되지 않은 분리막에 비해 약 2~3배로 높게 나타났다. 높게 나타났다.