To overcome the low mechanical strength and corrosion behavior of a carbon steel canister at high temperature condition of a deep borehole, SiC ceramics were studied as an alternative material for the disposal canister. In this paper, a design concept for a SiC canister, along with an outer stainless steel container, was proposed, and its manufacturing feasibility was tested by fabricating several 1/3 scale canisters. The proposed canister can contain one PWR assembly. The outer container was also prepared for the string formation of SiC canisters. Thermal conductivity was measured for the SiC canister. The canister had a good thermal conductivity of above 70 W·m-1·K-1 at 100℃. The structural stability was checked under KURT environment, and it was found that the SiC ceramics did not exhibit any change for the 3 year corrosion test at 70℃. Therefore, it was concluded that SiC ceramics could be a good alternative to carbon steel in application to deep borehole disposal canisters.

심지층 처분시스템에서 완충재는 지하수 유입으로부터 처분용기를 보호하고, 방사성 핵종 유출을 저지하기 위한 중요한 방 벽의 하나이다. 이에 완충재는 장기 건전성, 낮은 수리전도도, 낮은 유기물의 함량, 높은 핵종저지능, 높은 팽윤성, 높은 열 전도도 등 기술적 요건을 충족시켜야 하며 이는 정량적 분석결과를 바탕으로 결정될 수 있다. 국내의 경우 한국원자력연구 원에서는 1997년부터 경주지역에서 생산되는 벤토나이트를 완충재 후보물질로 연구를 지속하고 있다. 본 논문에서는 최근 동일 지역에서 생산된 벤토나이트(KJ-II)의 7가지 물리적 및 화학적 특성을 평가하였다. 분석 결과, 국내산 벤토나이트의 몬 모릴로나이트 함량은 약 65% 정도이며, 벤토나이트는 Ca형 벤토나이트이다. 본 논문을 통해 완충재 후보물질의 성능평가 항목과 분석 방법에 대한 기준을 제시하고자 하였다.