An author has been known that A-type zeolite supported with silver ions has excellent antibacterial activity. However, it is no research of concern in the antibacterial activity of eluted silver ions. This study tested the elution of silver ions from A-type zeolite silver ions in deionized distilled water and NaNO3 aqueous solution. In NaNO3 aqueous solution of 74mM to 588mM, it was found that the concentration of silver ions and electric conductivity increased with the increasing concentration of sodium ions, and equilibrated at 15 min, and the ion exchange equilibrium coefficient, k, is 1.3×10-3. However, deionized distilled water is not equilibrated to pass 6 months. A-type zeolite sodium ions showed no antibacterial activity. It was found that antibacterial activity was exhibited even at the concentration of 10 nM of eluted silver ions, and E-coli died with the incorporation of 2.43×108 Ag ion/cell. antibacterial activity of A-type zeolite silver ions were mainly attributed to hydroxyl radical.

Two different kinds of cases, with and without addition of noncrystalline silica to the Hadong kaolin were studied to obtain useful information on the synthesis of zeolite. The research was carried out to investigate the formation area and the crystalized degree of zeolite according to a synthetic time, the water content of raw material mixture, KOH concentration, and stirring intensity. In the case of without addition of noncrystalline silica to the Hadong kaolin and the low concentration range of KOH, the structure of the kaolin was not changed. However, when the mole ratio of K2O/SiO2 in natural kaolin was increased, Linde-L zeolite and unknown structure of kaolins, U-1 and U-2 were produced. While in the high concentration range of KOH, the unknown structure of kaolins, U-6 and U-2, were produced and the production rate of U-6 was increased with the increased of K2O/SiO2 mole ratio. In the case of with addition of noncrystalline silica to the Hadong kaolin and treatment with KOH hydrothermal processing, ZSM-5, ZSM-35, and Linde-L zeolites and the mixture of unknown structure of zeolites, U-1, U-2, U-3, and U-4, were obtained. Both cases demonstrated that the synthesis of zeolite from the Hadong kaolin was highly influenced by KOH concentration of raw material mixture.