Electrochemical surface treatment is commonly used to form a thin, rough, and porous oxidation layer on the surface of titanium. The purpose of this study was to investigate the formation of nanotubular titanium oxide arrays during short anodization processing. The specimen used in this study was 99.9% pure cp-Ti (ASTM Grade II) in the form of a disc with diameter of 15 mm and a thickness of 1 mm. A DC power supplier was used with the anodizing apparatus, and the titanium specimen and the platinum plate (3mm×4mm×0.1mm) were connected to an anode and cathode, respectively. The progressive formation of TiO2 nanotubes was observed with FE-SEM (Field Emission Scanning Electron Microscopy). Highly ordered TiO2 nanotubes were formed at a potential of 20 V in a solution of 1M H3PO4 + 1.5 wt.% HF for 10 minutes, corresponding with steady state processing. The diameters and the closed ends of TiO2 nanotubes measured at a value of 50 cumulative percent were 100 nm and 120 nm, respectively. The TiO2 nanotubes had lengths of 500 nm. As the anodization processing reached 10 minutes, the frequency distribution for the diameters and the closed ends of the TiO2 nanotubes was gradually reduced. Short anodization processing for TiO2 nanotubes of within 10 minutes was established.