As a pore precursor, carbon black with different content of 0 to 60 vol% were added to (Ba,Sr) powder. Porous (Ba,Sr) ceramics were prepared by pressureless sintering at for 1h under air. Effects of carbon black content on the microstructure and PTCR characteristics of porous (Ba,Sr) ceramics were investigated. The porosity of porous (Ba,Sr) ceramics increased from 6.97% to 18.22% and the grain size slightly decreased from to with increasing carbon black contents. PTCR jump of the (Ba,Sr) ceramics prepared by adding carbon black was more than , and slightly increased with increasing carbon black. The PTCR jump in the (Ba,Sr) ceramics prepared by adding 40 vol% carbon black showed an excellent value of , which was above two times higher than that in (Ba,Sr) ceramics. These results correspond with Heywang model for the explanation of PTCR effect in (Ba,Sr) ceramics. It was considered that carbon black is an effective additive for preparing porous based ceramics. It is believed that newly prepared (Ba,Sr) cermics can be used for PTC thermistor.

본 연구에서는 부분산화한 Ti 분말을 첨가한 BaTiO3계 세라믹스를 진공중 1350˚C에서 1 h 소결하여 제조하였다. 공기중 가열후 전기적 성질과 미세조직에 미치는 부분산화한 Ti분말 첨가량의 효과를 조사하였다. 그 결과, 5~7vol%의 부분산화한 Ti분말을 첨가한 반도성 BaTiO3계 세라믹스는 비정항의 변화크기가 105이상인 우수한 PTCR 특성을 나타내었고 또한, 고다공질과 미립화된 조직을 얻을 수 있었다. 5 vol%의 부분산화한 Ti 분말을 첨가한 BaTiO3계 세라믹스의 상대밀도와 입도는 각각 54%, 1.3 μm였다. 부분산화한 Ti 분말의 첨가에 의한 BaTiO3계 세라믹스의 PTCR 특성 발현은 입계에서의 산소 흡착에 기인하였는데, 이는 Heywang모델로써 설명할 수 있었다.