Two main parameters were examined such as CSA content and polymer-binder ratio to find effects on the strength, water absorption, chloride ion penetration depth, carbonation depth, length change and chemical resistance of polymer-modified mortar with CSA and EVA polymer powder (EVAPP). As results, compressive, flexural, tensile, adhesive strengths, and length change of the polymer-modified mortar with CSA and EVAPP increases with increasing CSA content and polymer-binder ratio, although the water absorption, chloride ion penetration depth, and carbonation depth decrease with increasing polymer-binder ratio and CSA content, and also the chemical resistance decreases. Such strength and durability development is attributed to the high tensile strength of EVA polymer and the improved bond between cement hydrates and aggregates because of the addition of EVAPP and CSA.

Nonlinear crack analysis was carried out to estimate crack behavior for caisson structures in various conditions such as wave load, salt attack and temperature change etc. Some kinds of modeling techniques were used to estimate exact solution with MIDAS FEA considering creep and drying shrinkage.

본 연구는 최적의 투수성과 보수성 및 압축강도를 갖는 보투수 포장체의 개발을 위한 것으로, 단입도의 골재 및 SAP를 사용함으로써 투수계수 및 보수성능의 개선은 물론 포장체의 온도저감효과가 있음을 확인하였다. 이를 위하여 단입도 골재의 입경및 SAP 첨가량에 따른 압축 및 휨강도에 대한 시험을 실시하였으며, 보투수 포장체의 투수성능 및 보수량에 대한 시험을 실시하였다. 시험결과 단입도 골재의 입경이 작아질수록, SAP 첨가량이 증가할수록 압축/휨 강도는 증가하였으며, 투수계수는 SAP 첨가량이 증가함에 따라 감소하였다. 한편, 보투수 포장체의 흡수율 및 보수량은 골재의 입경이 작아질수록, SAP 첨가량이 증가할수록 증가하였으며, 보투수 포장의 온도저감효과는 아스팔트포장에 비해 최대 20℃ 까지 저감됨을 알 수 있었다.