To develop a high capacity lithium secondary battery, a new approach to anode material synthesis is required, capable of producing an anode that exceeds the energy density limit of a carbon-based anode. This research synthesized carbon nano silicon composites as an anode material for a secondary battery using the RF thermal plasma method, which is an ecofriendly dry synthesis method. Prior to material synthesis, a silicon raw material was mixed at 10, 20, 30, 40, and 50 wt% based on the carbon raw material in a powder form, and the temperature change inside the reaction field depending on the applied plasma power was calculated. Information about the materials in the synthesized carbon nano silicon composites were confirmed through XRD analysis, showing carbon (86.7~52.6 %), silicon (7.2~36.2 %), and silicon carbide (6.1~11.2 %). Through FE-SEM analysis, it was confirmed that the silicon bonded to carbon was distributed at sizes of 100 nm or less. The bonding shape of the silicon nano particles bonded to carbon was observed through TEM analysis. The initial electrochemical charging/ discharging test for the 40 wt% silicon mixture showed excellent electrical characteristics of 1,517 mAh/g (91.9 %) and an irreversible capacity of 133 mAh/g (8.1 %).

폴리아닐린(polyaniline, PANI)과 도판트인 camphorsulfonic acid(CSA), dodecyl benzene sulfonic acid(DBSA)와 의몰비 변화에 따라 가상 n형 PANI을 제조하였다. FT-IR측정으로부터 도핑유무를 확인하였고, indium thin oxide(ITO)에 코팅하여 제조한 전극에 대해, 순환전압전류법과 교류임피던스법을 이용하여 도판트의 영향을 조사하였다. FT-IR과 순환전압전류법으로부터, 제조된 전극이 양이온의 도핑-탈도핑이 일어나는 가상 n형의 특성을 가짐을 확인하였다. 순환전압전류법에서 산화-환원 피크전류값은 PANI/DBSA에 비하여 PANI/CSA가 약 5 배정도 더 큰 결과를 보였다. 교류임피던스법으로부터, 두 전극 모두 이상적인 Randles의 등가회로와 유사한 거동을 보였다. 전하이동저항은 PANI/CSA에서 1.14~1.09 kΩ으로 거의 일정한 값을 보였고, PANI/DBSA는 DBSA 몰 비에 증가에 따라 27.73~8.37KΩ으로 감소하여 나타났다. 이중층용량 또한 PANI/CSA는 13.47~14.59 μF으로 거의 일정하였으나, PANI/DBSA는 DBSA 몰 비 증가에 따라 0.49~l.20 μF으로 증가를 보였다. 결과적으로 PANI/CSA의 전기적 특성이 더 좋았으나, 도판트의 몰 비 증가에 따른 특성은 PANI/CSA 전극은 거의 일정하였고, PANI/DBSA 전극은 전기적 활성이 좋아짐을 알 수 있었다.