The objective of this study is to investigate partial oxidation of NO with desulfurization in dry sorbent injection(DSI) process using dry sorbent and additives. The effect of the main operating variables directly related to desulfurization efficiency has been also tested. These variables are Ca/S ratio, temperature, inlet SO2 concentration and gas flow rate. The experiment was carried out for partial oxidation of NO with desulfurization in dry sorbent injection process using NaClO2 and CaCl2. The experimental results showed that partial oxidation of NO with desulfurization was increased in DSI process using little NaClO2. It was also found that the injection of CaCl2 was effective in increasing only SO2 removal efficiency. Increase of SO2 removal performance and promotion of partial oxidation of NO using the two additives at low temperature was confirmed.

본 연구에서는 복합 중공사 막을 이용하여 가스 중 수분(water vapor)의 제거에 관한 연구를 수행하였다. 막 소 재로는 PEI (Polyetherimide)를 사용하였고 건/습식 상전이 법을 이용하여 중공사 형태로 제조한 후, 표면에 PEBAX (Polyether block amides) 3533또는 PEBAX1657를 코팅하여 복합 중공사막을 제조하였다. 제조된 중공사 막에 대한 SEM 관찰을 통하 여 외부 표면에 치밀한 선택층과 망상구조의 하부로 이루어진 비대칭 구조임을 확인하였다. 막의 수분 투과특성을 확인하기 위하여 수분활성도(Water activity), 온도와 압력 변화에 따른 수분과 N2의 투과도를 측정하였다. PEBAX3533을 코팅한 복합 중공사 막의 수분 투과도는 운전 조건에 따라 385.6∼727.3 GPU, 수분/N2 선택도는 61.7∼118.5의 값을 나타내었다. PEBAX1657 코팅의 경우, 수분 투과도는 204.1∼562.1 GPU, 수분/N2 선택도는 85.3∼175.4의 값을 나타내었다. 막의 수분 제거율은 PEBAX3533 코팅한 경우에 90%를 나타내었다.